Pengaruh canai hangat terhadap sifat mekanik mg 1 6gd dengan metode canai menyilang dan canai searah sebagai biomaterial implan tulang = Effect of warm rolling of mg 1 6gd produced by cross rolling and single pass rolling methods to mechanical properties for biomaterial bone implant/ Rafika Diantika
Rafika Diantika;
Sigit Pranowo Hadiwardoyo, promotor; Bambang Suharno, supervisor; Andi Rustandi, examiner
([Publisher not identified]
, 2015)
|
|
ABSTRAK Pengembangan logam sebagai biomaterial implan tulang telah dimulai sejaklama dan terus berlanjut akibat sifatnya yang lebih unggul dibanding material lain.Logam yang saat ini menjadi perhatian untuk diaplikasikan sebagai implan adalahMg-Gd karena memiliki sifat mekanik yang hampir sama dengan tulang manusiadan kemampuan luruh yang tinggi. Perlakuan panas mempengaruhi kemampuanbentuk magnesium dan sifat mekanik yang dihasilkan. Penggunaan metode canaihangat yang berbeda bertujuan untuk melihat efektivitas tiap metode terhadapsifat mekanik yang dihasilkan. Proses canai hangat dilakukan pada temperatur0.3-0.4 Tm dengan cara pemanasan awal selama 5 jam pada suhu 560 oC denganpersen reduksi ketebalan 30%. Proses canai hangat menghasilkan prosesrekristalisasi dinamis yang mengecilkan ukuran butir dan penghilangan twin.Metode canai menyilang lebih efektif dibandingkan canai searah karenaterbentuknya presipitat Mg5Gd sehingga meningkatkan sifat mekanik materialseperti kekuatan tarik hingga 152.2 MPa dan kekerasan 66 HV. Metode canaimenyilang juga mengalami pengerasan regangan yang lebih tinggi dibandingkancanai searah hingga 0.503 hal ini disebabkan reduksi aktual dan pengecilanukuran butir yang lebih homogen sehingga interaksi antar dislokasi meningkatakibat densitas yang semakin rapat. ABSTRACT Metals development as biomaterial bone implant has begun since long timeago and still continued because its excellent properties compared to othermaterials. Metals that attract great attention as new biomaterial bone implant isMg-Gd because its similarities with human bones and good degradation.Thermomechanical treatment effects magnesium ability to deform and mechanicalproperties that produced. Different methods that used in this experiment wasproposed to see the effectiveness of each method to mechanical properties. Warmrolling was done at 0.3-0.4 Tm with preheating at 560 oC for 5 hours and 30% ofthickness reduction. Warm rolling produced dynamic recrystallization that refinegrains and eliminate twin. Cross rolling method proofs to be more effectivecompared to single pass rolling because of Mg5Gd precipitate that producedincrease Mg-Gd mechanical properties such as tensile strength up to 152.2 MPaand microhardness up to 66 VH. Cross rolling method also exhibit higher strainhardening compared to single pass roll up to 0.503 because of more homogenousgrain size and higher actual reduction caused denser dislocation which iscontributes to more intense interaction between dislocations |
 S58465-rafika diantika .pdf :: Unduh
|
| No. Panggil : | S58465 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Penerbitan : | [Place of publication not identified]: [Publisher not identified], 2015 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; Computer (rdadontent) |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xiii, 75 pages : illustration ; 29 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S58465 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20402479 |