Preparasi dan karakterisasi suspensi koloidal titanium dioksida berbasis medium air dengan metode anodisasi telah dilakukan. Proses anodisasi dilakukan dengan variasi voltase dan durasi, yaitu 25V (1,2 jam) dan 40V (1,2 jam). Produk suspensi koloidal kemudian dilapiskan ke kaca. Lapisan TiO2 pada permukaan kaca membuat kaca menjadi material yang memiliki kemampuan membersihkan diri sendiri (self celaning). Pelapisan dilakukan menggunakan metode spin coating. Karakterisasi suspensi kolidal TiO2 dan lapisan TiO2 dilakukan dengan PSA, Spektrofotometer UV-Vis, Spektrofotometer UV-VIS DRS, FT-IR, SEM, dan pengukuran sudut kontak air. Hasil PSA menunjukkan partikel TiO2 dalam suspensi koloidal memiliki diameter 106.4 nm. Kestabilan suspensi kolidal TiO2 berada pada periode 2 minggu.Hasil UV -VIS DRS menunjukkan kaca yang dilapisi suspensi kolidal TiO2 hasil anodisasi 40V 1 jam sebanyak 45X mempunyai band gap 3.24 eV; dan keberadaan puncak serapan IR pada panjang gelombang 678 cm-1 (indikasi adanya ~Ti-O-Ti~). Hasil SEM menunjukkan morfologi permukaan kaca yang menunjukkan adanya lapisan TiO2 yang menempel. Sudut kontak yang didapatkan pada saat illuminasi dengan lampu UV hampir<10° , menunjukkan kaca bersifat superhidrofilik. Kaca yang dilapisi oleh TiO2 mampu mendegradasi senyawa zat warna congo red hingga 59.09% dalam keadaan illuminasi dengan lampu UV selama 100 menit.
Preparation by anodization method and Characterization of Water Based TiO2 has been done. Anodizing process were conducted with variation of voltage and duration at 25V for 1,2 hour and 40V for1,2 hour respectively. The resulted colllidal suspension then were employed for coating of glass plate, by a spin coating method. The TiO2 layer on the surface of glass resulted the coated glass surface showing self cleaning properties. PSA dan UV VIS were used to characterize the colloidal suspension. While, UV-VIS DRS, FT-IR, SEM, and contact angle measurements were performed to characterize the surface of glass coated by TiO2. PSA showed TiO2 particle have a diameter of 106.4 nm, and showed a stability of the TiO2 colloidal suspension up to two weeks. UV VIS DRS show that the glass which was typically coated by TiO2 suspension has band gap of 3.24 eV, and showed the existence of the IR absorption peaks at wavenumber region 678 cm-1 (indication of the presence of -Ti-O-Ti). SEM image showed that TiO2 layer was attached on to glass surface. The TiO2 coated glass, when ilumintaed by UV light, showed having contact angle as low as <100 , indicated its superhydrphilic property. In addition, glass coated with TiO2 was able to degrade up to 58.91% congo red when illuminated by UV light for 100 minutes. |
S58349-Izayasa.pdf :: Unduh