Pengaruh %vf al2o3 dan grain refiner tib serta modifier sr terhadap karakterisasi komposit logam al356 al2o3 dengan metode stir casting = Fabrication and characterization composite al356 al2o3 with variation of volum fraction al2o3 and adition grain refiner tib also modifier sr by stir casting method
Mohamad Ivan Riansa;
Anne Zulfia, supervisor
(Fakultas Teknik Universitas Indonesia, 2014)
|
|
Penggunaan komposit logam banyak digunakan pada pesawat terbang, otomotif, dan transportasi dikarenakan memiliki sifat mekanis yang baik. Pada penelitian ini penambahan fraksi volum Al2O3 sebagai penguat sebesar 5%, 10%, 15%, dan 20% kedalam matriks logam Al356 dilakukan untuk melihat titik optimal penambahan partikel Al2O3. Penambahan grain refiner TiB dan modifier Sr dilakukan untuk melihat perubahan ukuran butir dan struktur Si secara kualitatif. Magnesium 10% ditambahkan untuk meningkatkan pembasahan antara partikel Al356 dengan penguat Al2O3. Proses fabrikasi dilakukan dengan metode pengecoran dan aduk karena memiliki nilai ekonomis dibanding dengan metode pengecoran lain.Hasil dari penelitian ini menunjukkan penambahan partikel Al2O3 dapat meningkatkan sifat mekanis dari aluminium terutama mencapai titik optimal pada fraksi volum 10%. Kekuatan tarik mencapai 162MPA dengan elongasi 7,67%, dan kekerasan mencapai 44,12 HRB. Pengamatan struktur mikro dilakukan dengan melihat dengan mikroskop optik dan SEM. Hasil pengamatan mikrostruktur menunjukkan adanya penghalusan butir matriks Al356 dan perubahan mikrostruktur Si dari lamelar menjadi berserabut. Peningkatan porositas terjadi seiring dengan penambahan fraksi volum Al2O3 yang menyebabkan turunnya sifat mekanis dari komposit Nowadays, using of metal composite for aircraft, automotive, and transportation has been chosen due to the good mechanical properties. The aim of this study was to look at the optimal point particle addition of Al2O3 with the addition of volume fraction of Al2O3 for 5%, 10%, 15%, and 20% into the aluminium Al356 as matrix. Besides, the addition of grain refiner TiB and modifier Sr performed to see the changes in grain size and structure of Si with qualitative method. 10% of magnesium was also added into this composite to increase the wet ability between matrix of Al356 and reinforcer of Al2O3. The fabrication process is done by stir casting method because its economic value compared to other casting methods.The result of this study shows that the addition of Al2O3 can increase the mechanical properties of aluminium, and it achieves the optimum point at the addition of 10% of volume fraction. The tensile strength reaches 162 MPA with 7,67% elongation, and the hardnessis 44,12 HRB. Microstructure observation was done by optical microscope and SEM. The result of observation of microstructure shows the increase of grain boundary of the matrix of Al356, and the change of the microstructure of Si from lamellar into fibrous. Increased of porosity happen along with the additions of the volume fraction of Al2O3 which led to the decreased of the mechanical properties of metal composite. |
 S57738-mohamad ivan riansa .pdf :: Unduh
|
| No. Panggil : | S57738 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2014 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | |
| Tipe Konten : | |
| Tipe Media : | |
| Tipe Carrier : | |
| Deskripsi Fisik : | xiii, 62 hlm. : ill. ; 29 cm. + lamp. |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S57738 | 14-19-757875480 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20402738 |