Preparasi, karakterisasi dan aktivitas fotokatalitik nanopartikel coupled oksida besi magnetite dan oksida seng untuk pewarna organik methylene blue = Synthesis, characterization and photocatalytic activity of coupled iron oxide magnetite and zinc oxide nanoparticles for methylene blue organic dye

Iqri`Ah Kalim; Rosari Saleh, supervisor (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014)

 Abstrak

Sampel nanopartikel coupled magnetite Fe3O4/ZnO dengan tiga variasi rasio molar disintesis dengan metode sol gel. Karakterisasi sampel dilakukan dengan menggunakan Field Emission Scanning Electron Microscope (FESEM), X-ray Diffraction (XRD), Electron Dispersive X-Ray (EDX), spektroskopi UV-Vis dan Vibrating Sample Magnetometer (VSM). Pengujian aktivitas fotokalitik dilakukan dengan mengamati degradasi larutan methylene blue (MB) sebagai model polutan organik di bawah penyinaran cahaya UV. Hasil analisis FESEM menunjukkan sampel nanopartikel coupled memiliki morfologi sferis. Hasil kurva XRD menunjukkan peningkatan intensitas seiring dengan meningkatnya rasio molar ZnO dalam nanopartikel coupled Fe3O4/ZnO. Keberadaan atom Fe, O dan Zn pada sampel nanopartikel coupled dikonfirmasi oleh spektrum EDX. Aktivitas fotokalitik yang paling baik ditunjukkan oleh sampel nanopartikel coupled rasio molar 1:5 dengan dosis sebanyak 20 mg/L pada kondisi pH 13. Nanopartikel Fe3O4 dan nanopartikel coupled Fe3O4/ZnO menunjukkan sifat feromagnetik yang memungkinkan sampel untuk dipisahkan secara magnetik dari dye methylene blue.

Nanoparticle coupled magnetite Fe3O4/ZnO with various molar ratio has been syntesized using sol gel method. Characterization using Field Emission Scannig Electron Microscope (FESEM), X-Ray Diffraction (XRD), Electron Dispersive X-ray (EDX), UV-Vis Diffuse Reflectance and Vibrating Sampel Magnetometer (VSM) were conducted to identify morphology, structure, composition, optical and magnetic properties of nanoparticle coupled Fe3O4/ZnO. Photocatalytic activity studied by observing methylene blue (MB) degradation under UV light irradiation. FESEM shows Fe3O4/ZnO has spherical shape. XRD result shows ZnO phase intensity in nanoparticle coupled increase as ZnO molar ratio increase. The peaks corresponding to Fe, O and Zn atom were observed using EDX spectra. Maximum degradation of methylene blue was showed by 20 mg/L nanoparticle coupled with molar ratio 1:5 at pH 13. VSM result shows Fe3O4 and nanoparticle coupled samples exhibit ferromagnetic behavior. Therefore, samples can easily seperate from methylene blue using external magnetic.

 File Digital: 1

Shelf
 S57813-Iqri Ah Kalim.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : S57813
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014
Program Studi :
Bahasa : ind
Sumber Pengatalogan :
Tipe Konten :
Tipe Media :
Tipe Carrier :
Deskripsi Fisik : xi, 44 hlm . ; 30 cm. ;xi, 44 hlm . ; 30 cm.
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S57813 14-18-537182318 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20402827