Pengaruh Dopan Ni Terhadap Perubahan Nilai Resistansi dan Rasio Magnetorersitansi pada Sampel La0.67Ba0.33Mn1-xNixO3 ( x = 0.0 ; 0.1 ; 0.2 ; 0.4) = The Effect of doping Ni to the resistivity and ratio magnetization on La0.67Ba0.33Mn1-xNixO3 ( x = 0.0 ; 0.1 ; 0.2 ; 0.4)
Marjuki Zulziar;
Budhy Kurniawan, supervisor
(Universitas Indonesia, 2015)
|
|
Sampel La0.67Ba0.33Mn1-xNixO3 dengan x = 0.0 ; 0.1 ; 0.2 ; 0.4 dari bahan La2O3, BaCO3, MnCO3, dan NiO disintesis dengan menggunakan metode solid state reaction. Keempat bahan dasar tersebut dihaluskan dengan menggunakan Planetary Ball Milling selama 25 Jam , dikompaksi, dikalsinasi dengan suhu 8000 selama 10 jam dan di sintering pada suhu 13500 selama 20 Jam. Identifikasi fasa dilakukan dengan difraksi sinar X dan refinement High Scorer Plus dan diperoleh fasa tunggal La0.67Ba0.33Mn1-xNixO3 yang memiliki struktur kristal Orthorombik. Pengukuran terhadap nilai resistivitas dan magnetoresistansi (MR) sampel diukur menggunakan FPP (Four Point Probe), sedangkan magnetisasinya diukur dengan menggunakan permaghrap. Disimpulkan bahwa semakin besar doping Ni yang diberikan pada sampel La0.67Ba0.33Mn1-xNixO3 membuat nilai resistivitas sampel meningkat dan nilai negative magnetoresistansi sampel mengalami peningkatan dengan hasil MR terbesar pada sampel x = 0.1 yaitu 1,54 %. La0.67Ba0.33Mn1-xNixO3 with x = 0.0 ; 0.1 ; 0.2 ; 0.4 of La2O3, BaCO3, MnCO3, and NiO sintetic using solid state reaction. The Fourth of basic matter are mixed with Planetary Ball Milling for 25 hours, compacted, calcination on 8000 C for 10 hours and sinter 13500 C for 20 hours. Phase identification is carried out Using XRD and High Scorer Plus. Refinement, resulting La0.67Ba0.33Mn1-xNixO3 Wich single phase for All x compotition. The have Orthorombik Crystal Structure. Measurement of resistivity and magnetoresitance (MR) using FPP (Four Point Probe), while magnetization is measured using permaghraph. We get that the bigger Ni doping the more increases of resistivity and for negative magnetoresitance generally is increase, except the biggest negative magnetoresitance is 1,54 % for x = 0.1 |
 T43982-Marjuki Zulziar.pdf :: Unduh
|
| No. Panggil : | T43982 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Universitas Indonesia, 2015 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resources |
| Deskripsi Fisik : | xv, 68 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| T43982 | 15-20-754932349 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20414221 |