Sintesis dan karakterisasi LiFePO4 berdoping vanadium untuk bahan katoda baterai lithium ion = Synthesis and characterization of vanadium doped LiFePO4 used as cathode for lithium ion battery
Dimas Yunianto Putro;
Nofrijon Sofyan, supervisor; Anne Zulfia, examiner; R. Bambang Jaya Bangkit, examiner
(Fakultas Teknik Universitas Indonesia, 2016)
|
|
Telah dilakukan sintesis katoda LiFePO4 dengan penambahan variasi Vanadium sebagai bahan aditif. Dalam penelitian ini bubuk LiFePO4 dibuat dengan LiOH, NH4H2PO4, dan FeSO4.7H2O sesuai stoikiometri melalui proses hidrotermal. Pada tahapan berikutnya, dilakukan pencampuran pelarut dan bubuk H4NO3V sebagai variasi dari katoda aktif bahan dan karbon hitam sebanyak 4% wt. Selanjutnya dilakukan proses hidrotermal untuk membentuk LiFePO4 murni dengan warna abu-abu terang. Setelah proses sintering, didapatkan hasil berwarna abu-abu gelap sebagai karakteristik partikel LiFePO4. Bahan katoda LiFePO4 murni disintesis pada suhu 180 °C dalam autoclave dengan waktu penahanan selama 20 jam dan selanjutnya disintering 750 °C dengan penahanan selama 4 jam. Hasil sintesis dikarakterisasi menggunakan analisis termal (STA), difraksi sinar-X (XRD), mikroskop elektron (SEM), dan sifat listrik melalui spektroskopi impendansi (EIS). Hasilnya memperlihatkan bahwa temperatur pembentukan LiFePO4 dari uji STA adalah antara 653,8 – 750,0 °C. Hasil XRD menunjukkan LiFePO4 memiliki struktur olivin dengan grup ruang ortorombik, sementara hasil SEM menunjukkan bahwa LiFePO4 berbentuk bulat dan teraglomerasi. Hasil uji EIS menghasilkan nilai impedansi atau hambatan sebesar 158 Ω untuk LiFePO4 murni hasil sintesis dan 59 Ω untuk LiFePO4 dengan doping vanadium 5%. Vanadium-doped LiFePO4 used as cathode for lithium ion battery has been suscessfully synthesized. In this work, LiFePO4 was synthesizwed from LiOH, NH4H2PO4, and FeSO4.7H2O at stoichiometric amount through a hydrothermal method. Vanadium was added in the forms of H4NO3V powder at concentration variations and 4% wt carbon black. The hydrothermal process has been successfully carried out to form a pure LiFePO4 with a light gray color. After the sintering process, a dark gray powder as the characteristics of LiFePO4 particles were obtain. Pure LiFePO4 was synthesized at 180 °C in an autoclave for 20 hours and was sintered at 750 °C for 4 hours. The craharacterization includes thermal analysis (STA), X-ray diffraction (XRD), electron microscope (SEM), and electrical impendance spectroscopy (EIS). The STA results showed that LiFePO4 formation temperature is at 653.8 – 750.0 °C. The XRD results showed LiFePO4 are having olivine structure with orthorhombic space group, whereas the SEM results showed that LiFePO4 has round shape with agglomerated microstructure. EIS test results showed impedance of 158 Ω for pure LiFePO4 and 59 Ω for LiFePO4 doped 5% vanadium. |
 S63806-Dimas Yunianto Putro.pdf :: Unduh
|
| No. Panggil : | S63806 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2016 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resources |
| Deskripsi Fisik : | xv, 44 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S63806 | 14-22-36266099 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20430432 |