ABSTRAK
Baja ODS (Oxide Dispersion Strenghtened) merupakan salah satu advancedmaterial yang memiliki struktur stabil dan tahan terhadap temperatur tinggi yangberguna sebagai aplikasi nuklir atau pembakaran biomassa. Dengan serbuk Fe, Cr,dan Y2O3, Paduan Baja ODS memiliki standard pengolahan yang terdiri atasatomisasi gas dari pre-alloy, mechanical alloying, perlakuan thermal/mekanis. Padapengolahan tipe powder metallurgy, pengolahan baja ODS masih perlu dikaji dalamhal homogenitas, dan mechanical properties, dengan menyelidiki baja ODS pascaperlakuan microalloying dengan ultrasonic pada media toulene. Perlakuandiberikan dalam bentuk serbuk dengan variabel amplitudo, kemudian tekanankompaksi pada 7500 hingga 8000 Psi, serta proses sintering yang dilakukan padasuhu 1300oC dengan proses I tahap yang ditahan selama 2 jam dan proses II tahappada suhu tahan 1000oC, dan 1300oC dengan masing-masing 1 jam tahan yangkemudian diteiti dengan SEM-EDS, XRD, microhardness, serta density. Hasil dariPenelitian ini menunjukkan bahwa Nilai kekerasan berada pada rentang 87,42 HVNHingga 163,77 HVN dengan nilai densitas serbuk, 5,13 gr/cc, 5,76 gr/cc, 5,23gr/cc, serta 5,5 gr/cc yang secara berurutan Sampel A hinga D. selain itu, hasilpenyelidikan menyebutkan bahwa, pada pengujian kompaksi, terjadi perbedaanNilai kekerasan sebesar 62,24 HVN. Kemudian, dari Hasil morfologi bongkah dariproses sintering, menghasilkan fasa Ferrite dengan struktur kristal Cubic yangmemiliki nilai homogenitas yang tinggi melalui pembuktian grafik XRD dengankomposisi Fe-Cr tertinggi pada amplitudo 40% 1-step sintering sebesar 94,5%.
ABSTRACT
ODS (Oxide Dispersion Strengthened) Steel is one of the AdvancedMaterial that has a stabilized structure and Heat Resistance as Nuclear Applicationor Combustion of Biomass. With the basic Element Fe-Cr-Y2O3, ODS Alloy SteelObtain standard of processing consisting Pre-Alloy, Mechanical Alloying, andMechanical/Thermal Treatment. In the type of Powder Metallurgy Processing,ODS Steel indicated a obstacles that need to discuss in the concern of Homogeneityand Mechanical Properties with investigating ODS Steel Characterization afterMicro alloying treatment with ultrasonic using Toulene as a media. The treatmentgiven by a various Amplitude, and then gain the Compacting Pressure from 7500Psi to 8000 Psi, also sintering Processes for the first step in 1300OC with 2 hours ofholding time, and the second one the 2 step of sintering process, which has holdingtime in 1000OC and 1300OC with 1 hours each. After that, the result of the processesbeing characterized by SEM-EDS, XRD, Micro hardness, and Density. Effect ofcompaction pressure prove the difference between pressure of compaction wasgiven by 62.24 HVN. the result of this research Prove that the range of Hardnessare from 87,42 HVN to 163,77 HVN in the manner score of density in powdershape, 5,13 gr/cc, 5,76 gr/cc, 5,23 gr/cc, and 5,5 gr/cc that sequentially from sampleA to D. the Bulk Morphology, as a result of sintering Process, describes Ferritewhich has cubic structure, contain high homogeneity result that proved by XRDgraph with highest composition of Fe-Cr at 40% amplitude in 1-step sintering in theamount of 94,5% |
S63092-Harum Andriadi Bayu Prakoso.pdf :: Unduh