Sintesis dan preparasi komposit fotokatalis nanotube bermagnit (Fe3O4/SIO2/TiO2-nanotube) untuk degradasi metilen biru = Syhntesis and preparation of nanotubes photocatalyst magnetic (Fe3O4/SIO2/TiO2-nanotube) for degradation of methylene blue / Paramitha Yunizar Sari

Paramitha Yunizar Sari; ([Publisher not identified] , 2016)

 Abstrak

ABSTRAK
Telah dilakukan studi degradasi secara fotokatalitik zat warna metilen biru
menggunakan fotokatalis nanotube bermagnet. Fotokatalis Fe3O4/SiO2/TiO2-
nanotube telah berhasil disintesis melalui proses heteroaglomerasi antara
Fe3O4/SiO2 dengan TiO2-nanotube pada pH 4,8. Fotokatalis TiO2 nanotube (TiO2-
NT) yang digunakan dalam komposit Fe3O4/SiO2/TiO2-nanotube terlebih dahulu
disintesis dengan menggunakan metode rapid breakdown anodization, dalam
elektrolit yang mengandung ion klorat, pada tegangan 15 volt selama 35 menit
dan suhu kalsinasi 450 0C selama 2 jam dengan kenaikan suhu 50 per menit. TiO2
nanotube dikompositkan dengan bahan magnetik dan silika menjadi
Fe3O4/SiO2/TiO2-nanotube agar lebih mudah diambil kembali dengan medan
magnet dari luar setelah pemakaiannya serta untuk meningkatkan sifat
adsorpsinya. Komposit dikarakterisasi dengan menggunakan FTIR, SEM-EDX,
XRD, UV Vis DRS, BET dan VSM. Uji kinerja fotodegradasi metilen biru
dilakukan pada suatu sistem reaktor fotokatalitik dengan sistem batch yang
dilengkapi dengan shaker, lampu UV 15 Watt selama 5 jam dan sampel hasil uji
kinerja dianalisis menggunakan spektrofotometer UV-Vis. Uji kinerja
fotodegradasi metilen biru dalam air menunjukan bahwa TiO2 nanotube 450 0C
dapat menurunkan konsentrasi metilen biru sebesar sebesar 96,43% dengan
konsentrasi awal 20 ppm. Fe3O4/SiO2/TiO2-nanotube dapat menurunkan
konsentrasi metilen biru sebesar 90,4%. Kelebihan komposit ini yaitu dapat
dikumpulkan kembali dari cairan limbah dengan bantuan medan magent luar
setelah proses selesai.

ABSTRACT
Study on photocatalytic degradation of methylene blue dye using a
magnetic nanotubes photocatalysts has been conducted. Photocatalyst
Fe3O4/SiO2/TiO2-nanotube has been successfully synthesized with
heteroaglomerasi process between Fe3O4/SiO2 with TiO2 nanotubes at pH 4.8.
Photocatalyst TiO2 nanotubes used in the composite Fe3O4/SiO2/TiO2-nanotube
synthesized by of rapid breakdown anodization method with an electrolyte
containing ions of chlorate, at a voltage of 15 volts for 35 minutes and the
calcination temperature of 450 0C for 2 hours as the temperature rises 5 0C per
minute. TiO2 nanotube with a magnetic material and silica into Fe3O4/SiO2/TiO2-
nanotube to be more easily taken back by the magnetic field from the outside after
use and enhance the adsorption properties. Composite were characterized using
FTIR, SEM-EDX, XRD, UV-Vis DRS, BET and VSM. Photodegradation of
methylene blue test performed on a photocatalytic reactor system with batch
systems equipped with shaker, 15 watt UV lamp for 5 hours and a sample
performance test results analyzed using UV-Vis spectrophotometer. The results of
the photodegradation experiment of methylene blue in water by using TiO2
nanotube 450 0C and Fe3O4/SiO2/TiO2 in the batch reactor with 1 g/L of catalyst
dose showed that of methylene blue can be eliminated as much as 96.43% and
90.4%. Fe3O4/SiO2/TiO2-nanotube can reduced the concentration of methylene
blue smaller than used TiO2 nanotube but the composite Fe3O4/SiO2/TiO2-
nanotube can be still recollected from water with assistance of external magnetic
field.

 File Digital: 1

Shelf
 S64599-Paramitha Yunizar Sari.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : S64599
Entri utama-Nama orang :
Entri tambahan-Nama badan :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2016
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xviii, 62 pages : illustration ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S64599 14-18-247529724 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20431833