Studi awal pembentukan gas hidrogen dari aqueous solution dengan sel fotoelektrokimia menggunakan sistem DSSCd TiO2 nanotube yang tersensitasi zinc-phorphirin = Preliminary study of hydrogen gas formation of aqueous solution with photoelectrochemical cell DSSC system using TiO2 nanotubes sensitized zinc phorphirinpreliminary study of hydrogen gas formation of aqueous solution with photoelectrochemical cell DSSCd / Fahmi Syafaat
Fahmi Syafaat;
Jarnuzi Gunlazuardi, supervisor; Ridla Bakri, examiner; Asep Saefumillah, examiner; Agustino Zulys, examiner; Endang Asijati Widijaningsih Ichsan, examiner
([Publisher not identified]
, 2016)
|
|
ABSTRAK Pada penelitian kali ini TiO2 nanotube dibuat dengan metode Rapid BreakdownAnodization menggunakan plat Ti dalam elektrolit HClO4 0,15 M. Serbuk TiO2dikalsinasi pada 4500 C selama 3 jam, dan dikarakterisasi dengan SEM, XRD, UV-VisDRS, FTIR and BET. Zinc-Phorphirin-Imide telah berhasil dilekatkan pada TiO2Nanotube dengan merendam TiO2 Nanotube ke dalam larutan Zinc-Phorphirin-imideselama 24 jam. zinc-Phorphirin bebas memperlihatkan karakteristik spektra serapan padadaerah cahaya tampak, yaitu 439 nm and 620 nm. Saat dilekatkan dengan TiO2-Nanotube terjadi pergeseran serapan padathe 421 nm dan 640 nm. Zinc-Phorphirin/TiO2electrode memperlihatkan respon arus yang baik pada daerah cahaya tampak denganphotocurrent density sebesar 1,1 mA/cm2. Saat fotoelektroda dirakit menjadi Solar Cell(DSSC), kurva I-V menunjukkan efisiensi fotokonversi dari Zinc-Phorphirin/TiO2DSSC sebesar 1,914% (frontside illumination) dan1,147% (backside illumination). ABSTRACT In this work, TiO2 Nanotube were prepared by rapid breakdown electro oxidation of Tifoil in electrolyte containing 0.15 M HClO4. Obtained TiO2 Nanotube bundling powderwas calcinated at 4500 C for 3 hrs, then was characterized by SEM, XRD, UV-Vis DRS,FTIR and BET. Zinc-Phorphirin-Imide dyes was deposited into TiO2 Nanotube byimmersion of TiO2Nanotube in Zinc-Phorphirin-imide solution for 24 hours. Free zinc-Phorphirin-Imide dyes shows characteristics absorbtion spectra in visble region, these are439 nm and 620 nm. While, when it was immobilized in to TiO2-Nanotube theabsorbtion peak shift to 421 nm and 640 nm. The Zinc-Phorphirin-Imide/TiO2 electrodeshowed excellent respond toward visible light with the typical photocurrent density of 1,1mA/cm2. When the fabricated photoelectrode was assemblied in a typical Dyes SensitizeSolar Cell (DSSC), the I-V curve showed photoconversion efficiency of the assembliedZinc-Phorphirin-Imide/TiO2 DSSC was 1,914% (frontside illumination) and 1,147%(backside illumination). |
 T44759-Fahmi Syafaat.pdf :: Unduh
|
| No. Panggil : | T44759 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | [Place of publication not identified]: [Publisher not identified], 2016 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xv, 93 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| T44759 | 15-18-678258076 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20433984 |