Pengaruh pemanasan terhadap struktur mikro dan sifat mekanik composite core = Effect of heat treatment on micro structure and mechanical properties of composite core
Taufan Krisdana Budi;
Azwar Maas, supervisor; Dewa Nyoman Adnyana, supervisor; Soehardjo Poertadji, supervisor; M. Yudi Masduky Sholihin, examiner; Myrna Arianti, examiner
([Publisher not identified]
, 2016)
|
|
ABSTRAK Selama lebih dari 100 tahun, steel core digunakan sebagai konduktor padakabel untuk memberikan ketahanan terhadap kekuatan tarik, mengurangi defleksike ground (sag) serta mampu mengakomodir rentang antar tiang yang cukuppanjang. Dalam perkembangannya, seiring dengan permintaan akan kebutuhanpeningkatan effisiensi dan kapasitas, telah ditemukan beberapa type darikonduktor dalam beberapa dekade terakhir. Type dari konduktor yang telahdikembangkan tersebut diklaim mampu, meningkatkan electrical capacity padatemperatur operasi yang tinggi dengan tingkat losses yang rendah. Konduktor inidiistilahkan dengan ACCC (Aluminum Conductor Composite Core) yang memilikiketahanan terhadap temperatur tinggi. Pada penelitian ini sifat mekanik daricomposite core ini diukur pada range temperatur 100 - 300°C selama 120 menituntuk tiap sampel dengan kenaikan temperatur tiap 50°C. Di atas temperatur150°C, terjadi penurunan sifat mekanik dari composite core akibat perubahanstruktur mikro dan berkurangnya sifat adhesive pada bagian interface. Sifatmekanik dari composite core ini menjadi bagian yang menentukan dalamaplikasinya untuk mendapatkan konduktor yang tahan terhadap temperatur tinggidengan defleksi yang cukup kecil. ABSTRACT For over one hundred years steel core strands have been used to increase thetensile strength and reduce thermal sag of bare overhead conductors toaccommodate longer spans between fewer or shorter structures. As demand forelectricity continues to grow, increasing the capacity and efficiency of existing orproposed transmission lines is becoming increasingly important. A new type ofconductor that have been developed are claimed to be capable, increasing theelectrical capacity at a high operating temperature with the loss rate is low. Theconductor is designated ACCC (Aluminum Conductor Composite Core) which isresistant to high temperature. In this research, the high temperature strength of theconductor is assessed. The strength of the composite core measured at 100°C to300°C within 120 minutes by 50°C increment. Above 150°C, the strength droppeddue to the phase change in the matrix which degraded the elastic properties anddecrease interface adhesion. The mechanical properties of the composite corehighlight the potential for the use of composite materials to produce overheadconductors with low sag at high temperatures |
 T46513-Taufan Krisdana Budi.pdf :: Unduh
|
| No. Panggil : | T46513 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | [Place of publication not identified]: [Publisher not identified], 2016 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xv, 60 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| T46513 | 15-18-147381038 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20434086 |