Pengaruh klorida terhadap ketahanan struktur material AlMg3 = Chloride effect on the resistance of AlMg3 material

Saragi, Elfrida; Bambang Soegijono, promotor; Geni Rina Sunaryo, supervisor; Budhy Kurniawan, examiner; Djonaedi Saleh, examiner; M. Yudi Masduky Sholihin, examiner ([Publisher not identified] , 2016)

 Abstrak

ABSTRAK
Paduan aluminium (AlMg3) digunakan pada reaktor nuklir terutama pada tangki
reaktor, beam tube dan komponen lainnya yang ada didalam kolam reaktor. Salah
satu reaktor yang menggunakan material AlMg3 adalah reaktor yang ada di Serpong.
Kolam reaktor berisi air sebagai media pendingin. Media pendingin didalam kolam
disebut Primer menggunakan air non mineral (air demin). Kualitas air yang
digunakan akan sangat berpengaruh terhadap integritas struktur, sistem dan
komponen reaktor. PH air pendingin primer sekitar 5,8 yang diizinkan sebesar 0.0528 ppm dan klorida (Cl) sebesar 0.049 ppm. Tujuan
penelitian ini adalah pengaruh klorida dan pH terhadap struktur material AlMg3. Ion
klorida mampu menghancurkan lapisan protektif material AlMg3 jika ion ini berada
di dalam air pendingin primer. Pengujian yang dilakukan adalah karakterisasi
material, pengujian korosi dan pengujian kekerasan. Pengujian korosi menggunakan
metode Tafel, uji kekerasan menggunakan metode Vickers. Hasil karakterisasi
material diperoleh bahwa pola difraksi sebelum dan setelah dilakukan pemanasan
adalah sama dan penyebaran seluruh unsur yang ada di dalam AlMg3 tidak merata.
Dengan konsentrasi larutan sebesar 5000 ppm (5% NaCl) diperoleh laju korosi pada
pH 5.5 sebesar 0.0532 mpy, ph 6.5 sebesar 0,0344 mpy dan pH 7.5 sebesar 0,081
mpy. Hasil uji kekerasan sebelum dan setelah dikorosikan adalah tidak berubah.
Besarnya adalah 45.48627 VHN. Peningkatan laju korosi masih jauh dibawah
ketentuan kategori korosi rendah (2 mpy). Dalam hal ini material AlMg3 masih aman
digunakan.

ABSTRACT
Aluminum alloy (AlMg3) is used in nuclear reactors, especially in the reactor tank,
beam tubes and other components that are in the reactor pool. One reactor using
AlMg3 material is existing reactors in Serpong. The reactor pool filled with water as
the cooling medium. The cooling medium in the pond called Primer using non
mineral water (demin water). The quality of water used will greatly affect the
integrity of the structures, systems and components of the reactor. Primary cooling
water PH 5.8 0.049 ppm. The purpose of this study was the effect of chloride and pH of the
material structure AlMg3. Chloride ions capable of destroying the protective layer
material AlMg3 if these ions are in the primary cooling water. This experiment is the
characterization of materials, corrosion testing and hardness testing. Corrosion testing
using Tafel method, Vickers hardness testing method. Material characterization
results showed that the diffraction pattern before and after heating is the same and the
deployment of all the elements that exist in AlMg3 uneven. With a concentration of
5000 ppm (5% NaCl) was obtained at pH 5.5 corrosion rate of 0.0532 mpy, pH 6.5 at
0.0344 mpy and pH 7.5 at 0.081 mpy. The results of hardness test before and after
corrosion is unchanged. The amount is 45.48627 VHN. The increase in the corrosion
rate is still far below the provision of low corrosion category (2 mpy). In this case the
material AlMg3 still safe to use.

 File Digital: 1

Shelf
 T46717-Elfrida Saragi.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : T46717
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2016
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xv, 74 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
T46717 15-18-918099077 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20434123