Pengaruh waktu aging terhadap sifat mekanis dan struktur mikro komposit Al-Mg-Si berpenguat partikel nano SiC melalui proses stir casting = The effects of aging time on mechanical properties and microstructure of Al-Mg-Si reinforced SiC nanoparticles through stir casting process

Amelia Syifa Herningtyas; Anne Zulfia, supervisor; Donanta Dhaneswara, examiner; Myrna Ariati Mochtar, examiner ([Publisher not identified] , 2016)

 Abstrak

ABSTRAK
Komposit aluminium 6061 dengan partikel penguat nano SiC sudah banyak dikembangkan untuk aplikasi yang membutuhkan sifat mekanis yang baik dengan densitas yang rendah. Dalam rangka mencapai performa yang lebih baik, perlakuan panas T6 diberikan untuk meningkatkan sifat mekanis material komposit. Pada penelitian ini dilakukan proses perlakuan panas T6 dengan variasi waktu aging 2 jam, 4 jam, 6 jam, 8 jam, dan 10 jam pada temperatur 175 oC. Solution treatment dilakukan pada temperatur 440 oC selama 1 jam. Hasil penelitian menunjukkan bahwa waktu optimum aging adalah 10 jam yang ditandai dengan hasil kekerasan paling tinggi yaitu sebesar 66,22 HRB dan laju aus paling rendah yaitu sebesar 1,09 x 10-6 mm3/mm. Pengaruh perlakuan panas T6 terhadap hasil uji tarik sangat rendah akibat adanya porositas. Hasil struktur mikro dari mikroskop optik dan SEM menunjukkan adanya fasa α-Al, Mg2Si biner (Al+Mg2Si), dan fasa intermetalik β-Al2Mg3.

ABSTRACT
Aluminum 6061 composites reinforced by SiC nanoparticles has been widely used for high performance applications with low denstity. In order to obtain a better performance, artificial aging is conducted to improve mechanical properties of composite. In this study, aging treatment was done with varying aging time: 2h, 4h, 6h, 8h, and 10h at 175 oC with solution treatment at 440 oC for 1h. The results showed that the optimum aging time was achieved by 10h with the highest hardness up to 66,22 HRB and wear rate reached the lowest value by 1,09 x 10-6 mm3/mm. Heat treatment process did not show a strong influence to tensile strength due to a porosity. OM and SEM observation exhibit α-Al and binary Mg2Si (Al+Mg2Si) phases, and intermetallic phases of β-Al2Mg3.

 File Digital: 1

Shelf
 S66580-Amelia Syifa Herningtyas.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : S66580
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2016
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xv, 62 pages : illustration ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S66580 14-17-511811677 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20444536