An efficient and rapid method for preparation of Au nanoparticles (Au-NP) has been developed by direct microwaveirradiation of metal precursor and alginate mixed solution in a single step. Here, alginate molecules act as both thereducing and stabilizing agents of Au-NP. The obtained nanoparticles were characterized by ultraviolet-visible (UVVis)spectroscopy, particle size analyzer, fourier transform infrared spectroscopy, and transmission electronmicroscopy. The nanoparticles have a spherical form and perfectly capped with alginate when using alginate and chloroauric acid (HAuCl4) precursor in the concentration range of 0.50 to 0.75% (w/v) and 0.40 mM, respectively. The use ofa lower concentration of alginate and/or higher concentration of HAuCl4 caused agglomeration to occur, therebyresulting in a bigger size of Au-NP and red shifting of surface plasmon resonance (SPR) peak to a higher wavelength.Sintesis Nanopartikel Au yang Distabilkan Alginat dengan Bantuan Gelombang Mikro. Sintesis nanopartikel Au(Au-NP) dengan metode yang cepat dan efisien dalam hitungan menit telah berhasil dilakukan dengan teknik iradiasimenggunakan gelombang mikro terhadap campuran garam prekursor dan alginat dalam satu langkah. Molekul alginatberperan sebagai pereduksi maupun penstabil Au-NP. Nanopartikel yang diperoleh dikarakterisasi dengan spektroskopiultraviolet-visible (UV?Vis), particle size analyzer, fourier transform infrared spectroscopy dan transmission electronmicroscopy. Nanopartikel yang diperoleh berbentuk bulat dan terlapisi sempurna oleh alginat pada rentang konsentrasialginat dalam rentang 0,50?0,75% (w/v) dan prekursor HAuCl4 0,20 mM. Pada konsentrasi alginat yang lebih rendahdan/atau konsentrasi HAuCl4 yang lebih tinggi, aglomerasi cenderung terjadi dan menghasilkan ukuran partikel Au-NPyang lebih besar serta pergeseran panjang gelombang surface plasmon resonance (SPR) ke nilai yang lebih besar. |