Sintesis dan karakterisasi hidrogel superabsorben kitosan- poli (N-vinil kaprolaktam) (PNVCL) dengan metode full-IPN (interpenetrating polymer network) = Synthesis and characterization of superabsorbent hydrogel chitosan-poly(N-vinyl caprolactam) (PNVCL) by full-IPN (interpenetrating polymer network) method
Adiyanti Firdausi;
Riswijanto, supervisor; Emil Budianto, supervisor; Budiawan, examiner; Agustino Zulys, examiner; Soleh Kosela, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014)
|
|
Metode IPN (Interpenetrating Polymer Network) baik semi maupun full IPNdapat digunakan untuk mensintesis hidrogel superabsorben (HSA) kitosan dan poli(N-vinil-kaprolaktam) (PNVCL) atau HSA kitosan-PNVCL. Pada metode full IPN jaringan polimer disintesis secara bertahap (sequential). Tahap pertama adalah sintesis jaringan polimer kitosan terikat silang asetaldehida dan homogenisasi dengan monomer N-vinil-kaprolaktam (NVCL) Tahap kedua adalah sintesis jaringan polimer PNVCL terikat silang N Nmetilenbisakrilamida (MBA) melalui polimerisasi radikal bebas monomer NVCL dengan inisiator amonium persulfat (APS) Hasil sintesis HSA kitosan-PNVCL full-IPN memiliki kekuatan struktur ikat silang dan kemampuan swelling yang baik Kekuatan struktur ikat silang meningkat dengan bertambahnya waktu reaksi, konsentrasi agen pengikat silang, inisiator, dan dipengaruhi rasio kitosan-PNVCL Kemampuan swelling HSA kitosan-PNVCL dengan kekuatan struktur ikat silang yang baik didapat pada rasio kitosan/PNVCL 70:30 (b/b %). HSA kitosan-PNVCL full-IPN memberikan persen derajat ikat silang yang tinggi (78,2%) dan kemampuan swelling yang baik (390,2%) Karakterisasi. The IPN (Interpenetrating Polymer Network) method, both semi and full IPN, can be used to synthesize chitosan and poly (N-vinyl-caprolactam) (PNVCL) superabsorbent hydrogels or HSA chitosan-PNVCL. In the full method of IPN polymer networks are synthesized sequentially. The first stage is the synthesis of crosslinked acetaldehyde chitosan polymer tissue and homogenization with N-vinyl-caprolactam (NVCL) monomer The second stage is synthesis of PNVCL polymer network bound by N Nmetilenbisakrilamida (MBA) through NVCL monomer free polymerization with ammonium persulfate (APS) initiator Synthesis of HSA chitosan-PNVCL full-IPN has crosslinked structure strength and good swelling ability The strength of crosslinking structure increases with increasing reaction time, concentration of crosslinking agent, initiator, and influenced by chitosan-PNVCL ratio Swelling ability of HSA chitosan-PNVCL with good cross-link structure strength is obtained at the chitosan / PNVCL ratio of 70:30 (b / b%). Full-IPN HSA chitosan-PNVCL gives a high percentage of crosslinking (78.2%) and good swelling ability (390.2%) Characterization Characterization. |
 S66888-Adiyanti Firdausi.pdf :: Unduh
|
| No. Panggil : | S66888 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xiv, 73 pages : illustration ; 30 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S66888 | 14-19-053109272 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20452859 |