Studi pengaruh suhu dan komposisi 4,4 metilenbis sikloheksil isosianat terhadap karakteristik hibrida biopolimer kompatibiliser berbasis lignin dan poliutretan = The study of influence of temperature and composition 4 4 methylenebis cyclohexyl isocyanate to characteristics of hybrid compatibiliser biopolymer based on lignin and polyurethane
Salma Ilmiati;
Mochamad Chalid, supervisor; Rini Riastuti, examiner; Sotya Astutiningsih, examiner; Jaka Fajar Fatriansyah, examiner
([Publisher not identified]
, 2017)
|
|
ABSTRAK Lignin adalah salah satu biopolimer terbanyak didunia. Lignin memiliki sisi polar dan nonpolar akibat struktur yang bercabang. Namun, berdasarkan penelitian sebelumnya, tendensi kepolaran lignin lebih besar dibandingkan kenonpolarannya. Lignin berpontensi sebagai kompatibiliser yang baik apabila kenonpolarannya dapat ditingkatkan. Penelitian ini bertujuan untuk mensintesis hibrida poliuretan berbasis lignin HPL untuk meningkatkan kenonpolaran lignin. HPL dihasilkan dari reaksi 4,4 39;- Methylenebis Cyclohexyl Isocyanate HMDI dengan variasi komposisi , PEG 6000 dan lignin. Variasi suhu ketika reaski dengan lignin juga dilakukan dengan variasi 80 hingga 100 C. Struktur HPL dikomfirmasi menggunakan nuclear magnetic resonance spectroscopy NMR dan fourier transform infrared spectroscopy FTIR . Berdasarkan NMR dan FTIR, HPL berhasil dihasilkan. NMR juga digunakan untuk menghitung rasio kepolaran HPL. Berdasarkan NMR, rasio kepolaran HPL menurun dari 0,069 ke 0,041 seiring meningkatnya komposisi HMDI. Peningkatan kenonpolaran juga dikonfimasi dengan tegangan permukaan hasil pengujian sessile drop. Tegangan permukaan HPL menurun seiiring dengan meningkatnya komposisi HMDI dengan nilai tegangan permukaan terkecil adalah 46,4 nM/m. Sifat termal HPL juga diuiji menggunakan STA. Berdasarkan STA, Td semakin meningkat seiring dengan meningkatnya komposisi dari HMDI dan suhu yang disebabkan oleh terbentuknya crosslinking. Nilai Td terbaik dimiliki oleh HPLE dengan nilai 417,6 C. ABSTRACT Lignin is one of the most abundant biopolymer on earth. It has polarity and non polarity side due to its hyperbranched structure, but the polarity of lignin has a higher tendency than non polarity. Lignin has potential to be compatibilizing agent if the portion of non polarity can be increased. This research is focused on investigation of synthesize lignin based polyurethane to enhance the portion of non polarity in lignin. Lignin based polyurethane was prepared by reacting 4,4 39 Methylenebis Cyclohexyl Isocyanate HMDI with variation compositions and polyethylene glycol PEG Mw 6000, then lignin was added to the reaction. The temperature of reaction for lignin also variated between 80 to 100 C. In this study, the structure of lignin based polyurethane was confirmed by nuclear magnetic resonance spectroscopy NMR and fourier transform infrared spectroscopy FTIR . NMR and FTIR showed that lignin successfully grafted. NMR, also used to investigated the effects of variation composition of diisocyanate contents to polarity of lignin based polyurethane. Based on NMR the ration p np decrease from 0.069 to 0,041 with the increasing of composition HMDI. The enhance of nonpolarity HPL also confirm by the value of surface tension from sessile drop. it show that the surface tension of HPL decline as the increasing of the composiiton of HMDI. The best serface tension was from HPLE with 46.4 nM m. Thermal properties of lignin based polyurethane also investigate using STA. The result was the increasing of thermal degradation of lignin based polyurethane as well as the increasing of composition HMDI and temperature condition, cause of the crosslingking in lignin. Td largest value is 417,6 C from HPLE |
 T47836-Salma Ilmiati.pdf :: Unduh
|
| No. Panggil : | T47836 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | [Place of publication not identified]: [Publisher not identified], 2017 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xiv, 67 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| T47836 | 15-21-886130022 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20454551 |