Pengaruh konsentrasi larutan asam nitrat sebagai larutan lindi terhadap peningkatan kadar tantalum pentaoksida dan niobium pentaoksida dalam terak timah i = Effect of concentration of nitric acid solution as leaching reagent to increasing grades of tantalum pentaoxide and niobium pentaoxide in tin i slag

Ahmad Fadli; Johny Wahyuadi Soedarsono, supervisor; Sutopo, examiner; Sulaksana, examiner; Ahmad Maksum, examiner (Fakultas Teknik Universitas Indonesia, 2017)

 Abstrak

Terak timah merupakan produk sampingan hasil proses pengolahan dan peleburan bijih timah di mana mengandung banyak mineral berharga, antara lain tantalum dan niobium. Penelitian ini bertujuan untuk melihat pengaruh konsenstrasi larutan HNO3 sebagai pelindi terhadap peningkatan kadar tantalum pentoksida dan niobium pentoksida dalam terak timah. Terak timah yang digunakan pada penelitian ini adalah terak timah I Indonesia dengan kandungan 0.30 Ta2O5 dan 0.58 Nb2O5. Pemanggangan pada temperatur 900 C dan pencelupan dengan media larutan NaOH dilakukan terhadap terak timah, kemudian analisa XRF.
Hasil analisa menunjukkan terak timah ukuran butir 100 dengan kadar 0.10 Ta2O5 dan 0.20 Nb2O5 memiliki kadar senyawa pengikut paling sedikit sebesar 62.70 . Keseluruhan penelitian memperoleh kadar Ta2O5 tertinggi sebesar 0.35 pada terak timah hasil pelindian HNO3 8 M dan kadar Nb2O5 tertinggi sebesar 0.67 pada terak timah hasil pelindian HNO3 6 M.

Tin slag is a byproduct result of processing and smelting of tin ore which contains many valuable minerals, including tantalum and niobium. This research aims to look the effect of concentration of HNO3 solution as leaching reagent to increase the content of tantalum pentoxide and niobium pentoxide in tin slag. Tin slag used in this research was Indonesian tin I slag containing 0.30 Ta2O5 and 0.58 Nb2O5. Roasting at temperature of 900 C and quenching with NaOH solution were done to the tin slag, then XRF analysis.
The analysis showed tin slag grain size 100 with grades of 0.10 Ta2O5 and 0.20 Nb2O5 had the least grade of adherent compounds in the amount of 62.70 . Overall the research obtained the highest grade of Ta2O5 in the amount of 0.35 in tin slag leached with HNO3 8 M and the highest grade of Nb2O5 0.67 in tin slag leached with HNO3 6 M.

 File Digital: 1

Shelf
 S67985-Ahmad Fadli.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : S67985
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2017
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiii, 67 pages : illustration ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S67985 14-19-385492442 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20456537