Sifat penyerapan gelombang mikro pada material La0,8Ca0,2-xAgxMnO3 (x= 0; 0,05; 0,10; 0,15) yang disintesis menggunakan metode sol-gel = Microwave absorption property of La0,8Ca0,2-xAgxMnO3 (x= 0; 0,05; 0,10; 0,15) material synthesized by sol gel method

Wilujeng Laksmi; Budhy Kurniawan, supervisor; Azwar Manaf, examiner; Nurlely, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2017)

 Abstrak

Telah dilakukan penelitian mengenai sifat penyerapan gelombang mikro material La0.8Ca0.2-xAgxMnO3 x= 0;0,05;0.1;0,15 yang termasuk golongan material perovskit manganat. Material disintesis menggunakan metode sol gel, kemudian dilakukan kalsinasi pada suhu 550?C, dan sintering di suhu 900?C. Karakterisasi XRD menunjukkan bahwa sampel berada dalam fasa tunggal. Dilakukan uji SEM yang menunjukkan morfologi sampel serta EDX yang menampilkan kemurnian sampel.
Pengujian menggunakan magnetometer kriogenik menunjukkan penurunan resistivitas bahan. Sampel telah dikonfirmasi ulang menggunakan uji ESR, untuk melihat konsenterasi elektron bebas pada sampel. Terakhir, sampel diuji menggunakan VNA untuk mengetahui Refleksi hilang, permittivitas dan permeabilitas bahan, dengan RL paling tinggi sebesar -4,965 dB.Kata kunci: Perovskit manganat, Sol Gel, Refleksi Hilang, Permitivitas, Permeabilitas.

The research about microwave absorption property of La0.8Ca0.2 xAgxMnO3 x 0 0.05 0.10 0.15 material is reported. The material synthesized by sol gel method, calcinated at 550 C and sintered at 900 C. According to XRD characterization, all samples were single phase. By SEM characterization the morphology of the samples are reported. EDX confirmed that all the samples have a good compositional purity.
Cryogenic magnetometer reported that Ag dopant caused the resistivity of materials generally decreased. ESR confirmed that Ag dopant also caused concentration of free electrons were increase. Finally VNA characterization reported the Reflection Loss, permittivity, and permeability, which the maximum RL is 4.965 dB.

 File Digital: 1

Shelf
 S67715-Wilujeng Laksmi.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : S67715
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2017
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiv, 54 pages : illustration ; 30 cm
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S67715 14-19-197172820 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20456561