Studi pengaruh penambahan Na2SO4 terhadap kenaikan kadar nikel pada reduksi selektif bijih nikel laterit = Study of the effect of Na2SO4 addition on increasing of nickel concentration on selective reduction of lateritic nickel ore
Rinanda Rahmat;
Johny Wahyuadi Soedarsono, supervisor; Sutopo, examiner; Ahmad Maksum, examiner
(Fakultas Teknik Universitas Indonesia, 2017)
|
|
Penelitian ini bertujuan untuk mengetahui pengaruh penambahan sulfur dalam bentuk Na2SO4 terhadap kenaikan kadar nikel pada reduksi selektif nikel laterit. Sampel yang digunakan adalah laterit dengan kadar nikel yang rendah dengan menggunakan batu bara sebagai reduktor dan Na2SO4 sebagai aditif sekaligus parameter utama serta bentonit sebagai pengikat. Dari hasil pengujian AAS setelah reduksi pada suhu 1000oC selama kurang lebih 5 jam termasuk waktu pendinginan didapatkan kadar nikel yang lebih rendah daripada kadar bijih nikel laterit sebelum direduksi, hal ini disebabkan karena waktu yang terlalu lama yang digunakan dalam proses reduksi sehingga reduktor terlanjur habis sebelum reaksi berakhir. Akan tetapi dari hasil AAS dengan variasi penambahan 0 , 5 , 10 dan 15 Na2SO4 didapatkan bahwa kadar nikel pada reduksi dengan adanya penambahan Na2SO4 mampu memberikan kadar nikel yang lebih tinggi dibandingkan reduksi tanpa penambahan Na2SO4. Kadar tertinggi ditunjukkan pada reduksi dengan penambahan 5 Sulfur. Sedangkan dari hasil pengujian diketahui hematit sudah tereduksi menjadi magnetit dan wustit, dan pada penambahan Na2SO4 diketahui terbentuk NiS dan FeS. This study aims to determine the effect of sulfur addition in the form of Na2SO4 on the increase of nickel concentration on selective reduction of lateritic nickel ore. The lateritic nickel ore that used in this study has the small concentration of nickel and use coal as a reductor, Na2SO4 as an additive and primary parameter and bentonite as a binder. By the AAS result, the nickel concentration from selective reduction with 1000oC temperatur for 5 hours include the cooling of sample is lower than nickel concentration in the ore, it may cause by the time that too long during reduction so the reductor was wear out before the reaction is over. Meanwhile, from AAS result with the variation of Na2SO4 in 0 , 5 , 10 and 10 , the sample that has been added with Na2SO4 give the hinger concentration of nickel than reduction without Na2SO4 addition. Peak formed from XRD show that the reduction process can reduce hematite or magnetite to wustite. With the addition of Na2SO4 the peak formed from XRD show NiS and FeS. |
 S67705-Rinanda Rahmat.pdf :: Unduh
|
| No. Panggil : | S67705 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2017 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xii, 35 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S67705 | 14-19-930725342 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20456763 |