Perancangan sel surya crystalline silicon dengan AlxGa1-xAs sebagai heterojunction with compound thin layer = Crystalline silicon solar cell design with AlxGa1-xAs as heterojunction with compound thin layer
Syam Erast Prayoga;
Nji Raden Poespawati, supervisor; Retno Wigajatri Purnamaningsih, examiner; Arief Udhiarto, examiner
(Fakultas Teknik Universitas Indonesia, 2017)
|
|
Sel surya telah melalui berbagai tahap pengembangan. Silikon merupakan salah satu bahan utama dalam komersialisasi sel surya. Sel surya crystalline silicon heterojunction with intrinsic thin layer HIT merupakan salah satu aplikasi silikon yang berhasil menghasilkan efisiensi tinggi. Alternatif lain yang bisa dilakukan adalah dengan menggabungkan silikon dengan material compound III-V atau disebut sebagai sel surya crystalline silicon heterojunction with compound thin layer HCT. Sel surya crystalline silicon HCT mampu memberikan alternatif, baik dari segi fabrikasi maupun efisiensi, dibandingkan dengan sel surya crystalline silicon HIT. n-AlGaAs digunakan sebagai alternatif dari n-AlAs pada sel surya crystalline silicon HCT. Jika dibandingkan dengan AlAs, AlGaAs mempunyai nilai lattice constant yang lebih sesuai dengan silikon. Penggunaan metode step grading pada material AlxGa1-xAs dilakukan dengan tujuan untuk meningkatkan efisiensi sel surya. Rancangan sel surya crystalline silicon HCT dilakukan dengan menggunakan perangkat lunak wxAMPS. Dari hasil simulasi didapat arus hubung singkat Jsc sebesar 16,64 mA/cm2; tegangan hubung terbuka Voc sebesar 1,05 V; fill factor sebesar 95,09 ; dan efisiensi 16,64 . Selain itu hasil simulasi menunjukkan penggantian tipe doping dari tipe p ke tipe n menghasilkan kenaikan efisiensi lebih besar pada sel surya HCT n-AlGaAs terhadap sel surya HCT p-AlGaAs, yaitu 11,84 ; sedangkan nilai fill factor mengalami kenaikan sebesar 16,05. Solar cell has been through many development phases. Silicon is a one of many important material in solar cell manufacturing. Heterojunction with intrinsic thin layer HIT crystalline silicon solar cell is one of silicon solar cell applications, which can produce high efficiency. An alternative to HIT crystalline silicon solar cell is Heterojunction with compound thin layer HCT crystalline silicon solar cell where silicon is coupled with III V semiconductor compound. HCT crystalline silicon solar cell could be an alternative either from fabrication process or efficiency value compared to HIT crystalline silicon solar cell. n AlGaAs is used as an alternative from n AlAs on HCT crystalline silicon solar cell. Compared to AlAs, lattice constant of AlGaAs is more suitable to the silicon. Step grading method is used for AlxGa1 xAs surface to increase solar cell efficiency. wxAMPS is used as simulation tool to achieve maximum design optimization for HCT crystalline silicon solar cell. Simulation results show that HCT crystalline silicon solar cell produce short circuit current Jsc value is 16.64 mA cm2, open circuit voltage Voc value is 1.05 V, fill factor value is 95.09, and efficiency value is 16.64. Simulation also shows a change from p type to n type dopant, result a significant efficiency increase for HCT n AlGaAs solar cell compared to HCT p AlGaAs solar cell, which is 11.84, in conjunction with its fill factor value, which increase 16.05. |
 S67448-Syam erast prayoga .pdf :: Unduh
|
| No. Panggil : | S67448 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2017 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xii, 49 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S67448 | 14-19-064483115 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20457056 |