Modifikasi permukaan limbah grafit menggunakan CeO2 sebagai adsorben gas CO2 = Modification surface of waste graphite using CeO2 for adsorption of carbon dioxide

Chairani Shafira Utami; Eny Kusrini, supervisor; Nasruddin, supervisor; Sukirno, examiner; Elsa Anisa Krisanti, examiner ([Publisher not identified] , 2017)

 Abstrak

ABSTRAK
Dalam penelitian ini limbah grafik dipretreatment dengan proses mekanik dan termal lalu dilakukan modifikasi grafit berbasis CeO2 untuk meningkatkan kapasitas penyerapannya terhadap gas CO2. Pretreatment dilakukan dengan menghaluskan partikel menjadi ukuran seragam 200 mash 75 m , kemudian dipanaskan dalam oven 110 C selama 6 jam. Grafit diaktivasi dengan larutan HNO3, kemudian dimodifikasi menggunakan CeO2 melaui metode presipitasi. Variasi CeO2 yang digunakan yaitu 0,5, 1 dan 2 g. Daya adsorpsi dari grafit/CeO2 diuji dengan menggunakan alat uji adsorpsi CO2. Pengujian dilakukan dengan variasi temperatur 30, 35 dan 45 C dengan setiap suhu diambil data pada variasi tekanan 3, 5, 8, 15 dan 20 bar menggunakan metode volumetrik. Karakterisasi yang digunakan yaitu BET, FTIR dan SEM-EDX. Hasil BET menunjukkan bahwa luas permukaan terbaik didapatkan dari grafit/CeO2 2 g yaitu sebesar 26,82 m2/g. Data FTIR dan SEM-EDX menunjukkan adanya kandungan serium dalam grafit modifikasi. Kapasitas adsorpsi grafit sebelum modifikasi yaitu 0,0713 kg/kg pada 30 C dan 20 bar. Kapasitas maksimum yang diperoleh setelah modifikasi adalah 0,1574 kg/kg pada 30 C dan 20 bar dari grafit/CeO2 0,5 g. Adanya peningkatan kapasitas penyerapan CO2 sebelum dan sesudah modifikasi dalam penelitian ini memperluas penerapan potensial untuk pemisahan CO2.
ABSTRACT
In this research, the waste of graph be processed through pretreatment with mechanical and thermal process and then modified graphite based CeO2 to increase its absorption capacity to gas CO2. Pretreatment is done by smoothing the particles into a uniform size of 200 mash 75 m , then heated in a 110 C oven for 6 hours. Graphite is activated with HNO3 solution, and then modified using CeO2 by precipitation method. Variations of CeO2 used were 0.5, 1 and 2 g. The adsorption power of graphite CeO2 was tested using a CO2 adsorption instrument. The test was carried out with temperature variations of 30, 35 and 45 C with each temperature taken data at a pressure variation of 3, 5, 8, 15 and 20 bars with volumetric method. Characterization used is BET, FTIR and SEM EDX. The BET results showed that the best surface area was obtained from Graphite CeO2 2 g of 26.82 m2 g. FTIR and SEM EDX data indicate the presence of cerium in modified graphite. The graphite adsorption capacity before modification is 0.0713 kg kg at 30 C and 20 bars. Maximum capacity obtained after modification is 0.1574 kg kg at 30 C and 20 bars of Graphite CeO2 0.5 g. The increase in CO2 adsorption capacity before and after modification in this study would broaden its potential applicability for CO2 separation.

 File Digital: 1

Shelf
 S67226-Chairani Shafira Utami.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : S67226
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2017
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiii, 50 pages : illustration ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S67226 14-19-928213942 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20457062