Optimasi performa anoda Li4Ti5012 pada baterai ion litium dengan penambahan silikon oksikarbida dari sintesis oli silikon = Optimized performance of Li4Ti5012 anode for lithium ion battery with silicon oxycarbide synthesized from silicon oil
Musthafa Mursyid;
Bambang Priyono, supervisor; Badrul Munir, examiner; Nofrijon Sofyan, examiner
([Publisher not identified]
, 2017)
|
|
ABSTRAK Li4Ti5O12 lithium titanate merupakan salah satu material anoda yang mempunyai performa yang cukup baik karena tidak mengalami SEI Solid Electrolyte Interface . Li4Ti5O12 disintesis menggunakan metode sol-gel dan Solid state dengan memakai sumber ion lithium LiCO3. SiOC merupakan material keramik yang disintesis dari silicon oil untuk memperbaiki kelemahan Li4Ti5O12. Silikon oil dicampurkan secara langsung dengan Li4Ti5O12 dan diaduk didalam beaker glass, kemudian dilakukan pemanasan pada suhu 350oC.. XRD menunjukan adanya fasa spinel LTO, TiO2 dan dengan kadar Si kristalin sangat sedikit. Melalui perhitungan didapatkan ukuran partikel Li4Ti5O12 sebesar 0,08 ?m. SEM-EDX menunjukan persebaran unsur-unsur pada sampel, dimana Si, C, dan O merupakan unsur utama penyusun SiOC. Pada pengujian EIS, penambahan kadar silicon oil menyebabkan Nilai hambatan dari material anoda LTO meningkat artinya konduktivitas dari material anoda mengalami penurunan. Pada pengujian CV, penambahan kadar silicon oil menurunkan kapasitas spesifik dari baterai, disebabkan oleh penurunan kualitas LTO ketika dilakukan pemanasan lanjut dan terbentuknya produk samping pengotor dari silicon oil tersebut yang menghambat pergerakan ion litium ketika proses litiasi dan delitiasi. ABSTRAK Li4Ti5O12 lithium titanate is one of the most promising material for anode, because reducing the form of SEI. Li4Ti5O12 were synthesized by sol gel and solid state method with LiCO3 as lithium ion source. SiOC is a ceramic material that synthesized from silicon oil to overcome the weakness of Li4Ti5O12. Silicon oil is adding to Li4Ti5O12 powder and mixed in the beaker glass, subsequently heated at 350oC. XRD shows the existed of LTO spinel, TiO2 and small amount of Si crystalline. From calculation the size of Li4Ti5O12 particle is measured the value is 0,08 m. SEM EDX shows the distribution of element on the sample, where Si, O, and C are the main element that construct the SiOC ceramic. The lowest electrolyte resistance obtained at pure Li4Ti5O12. With the increasing silicon oil value, the specific capacity of battery decreased from CV. It is because of heated the quality of Li4Ti5O12 is decreased and forming a side product that inhibit the movement of lithium ion during lithiation and delithiation. |
 S68032-Musthafa Mursyid.pdf :: Unduh
|
| No. Panggil : | S68032 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | [Place of publication not identified]: [Publisher not identified], 2017 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xiii, 46 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S68032 | 14-19-955685217 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20457153 |