Karakterisasi LiFePO4/V berlapis karbon dari karbon aktif tempurung kelapa untuk katoda baterai lithium ion = Characteristics of LiFePO4/V carbon coated from activated carbon of coconut shell used for lithium ion battery cathode
Audiya Dewi Rachmawati;
Nofrijon Sofyan, supervisor; Anne Zulfia, examiner; Bambang Prijono, examiner
(Fakultas Teknik Universitas Indonesia, 2017)
|
|
Telah dilakukan sintesis katoda LiFePO4/V berlapis karbon dari karbon aktif tempurung kelapa untuk katoda baterai lithium ion. Prekursor yang digunakan adalah LiOH, NH4H2PO4, dan FeSO4.7H2O dibuat melalui proses hidrotermal. Selanjutnya, dilakukan pencampuran karbon dari karbon aktif tempurung kelapa sebanyak 4 dan variasi vanadium serbuk yang bersumber dari H4NO3V. Campuran LiFePO4/V/C dikarakterisasi menggunakan analisis termal STA untuk menentukan temperatur sintering. Hasilnya sintesis terjadi pada temperatur di atas 681,950C dan serbuk berwarna abu-abu gelap sebagai karakteristik dari LiFePO4. Kemudian proses sintering dilakukan pada temperatur 8500C selama 4 jam. Serbuk LiFePO4 sintesis dikarakterisasi menggunakan difraksi sinar-X XRD, mikroskop elektron dan pendeteksi unsur SEM-EDS serta sifat listrik melalui spektroskopi impedansi EIS. Hasil XRD menunjukkan LiFePO4/V/C telah terbentuk dengan struktur berbasis olivin. Hasil SEM-EDS menggambarkan partikel yang teraglomerasi dan LiFePO4/V telah terlapisi karbon. Hasil EIS menunjukkan konduktivitas sebesar 5,33 x 10-5 S/cm untuk LiFePO4/C tanpa vanadium dan 6 x 10-6 S/cm untuk LiFePO4/C dengan doping vanadium 5. Activated carbon from coconut shell has been used as an additive to form LiFePO4 V C composite for lithium ion battery cathode. Lithium iron phosphate LFP was synthesized from the precursors of LiOH, NH4H2PO4, and FeSO4.7H2O via hydrothermal method. The LiFePO4 V C composite was formed by adding various vanadium concentration 0, 3, 5, 7 at. and a fix concentration of carbon 4 wt. Thermal analysis STA was used to characterize the formation of LFP and the transition temperature of the composite from which a transition temperature of 681.950C was obtained. X ray diffraction XRD was used to characterize the crystal structure, whereas scanning electron microscope SEM equipped with energy dispersive X ray spectroscopy EDX was used to characterize the morphology and composition of the composite. The conductivity of the composite was examined using electrical impendance spectroscopy EIS. The XRD results showed that LiFePO4 V C has an olivine structure with Pnmb space group. The SEM EDX results depicted aglomerate particles but most LiFePO4 V has been coated by carbon. EIS test results showed a conductivity of 5.33 x 10 5 S cm for LiFePO4 C with no vanadium and 6.0 x 10 6 S cm for 5 wt. vanadium doped LiFePO4 V C. |
 S68917-Audiya dewi rachmawati .pdf :: Unduh
|
| No. Panggil : | S68917 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2017 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xiv, 60 pages : illustration ; 29 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S68917 | 14-19-981216213 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20457176 |