Optimasi performa katoda baterai lithium iron phosphate (LIFePo4) doping vanadium dengan coating karbon aktif dari bambu = Optimizing performance of lithium iron phosphate (LIFeP04) cathode vanadium doping with activated carbon coating from bamboo
Subkhan Alfaruq;
Anne Zulfia, supervisor; Nofrijon Sofyan, examiner; Bambang Priyono, examiner
(Fakultas Teknik Universitas Indonesia, 2017)
|
|
Telah dilakukan sintesis LiFePO4 melalui metode hidrotermal dengan penambahan variasi vanadium dan pelapisan karbon aktif dari bambu untuk katoda baterai litium ion. Pada sintesis LiFePO4, bahan dasar yang digunakan adalah serbuk LiOH, NH4H2PO4 dan FeSO4.7H2O yang diukur sesuai stokiometri dengan perbandingan molar 2:1:1. Setelah proses sintesis, dilakukan penambahan variasi vanadium yang berbahan dasar H4NO3V dan pelapisan karbon aktif yang berasal dari bambu sebanyak 4 wt. Pencampuran dilakukan menggunakan ball-mill lalu dikarakterisasi menggunakan analisis termal STA untuk menentukan temperatur sintering. Hasil STA menunjukkan bahwa transisi fasa mulai terjadi pada temperatur 639°C yang kemudian menjadi acuan untuk menentukan proses sintering. Hasil sintering selanjutnya dikarakterisasi menggunakan difraksi sinar-X XRD, mikroskop elektron SEM, dan spektroskopi impedansi EIS. Hasil karakterisasi dengan XRD menunjukkan bahwa fasa LiFePO4 yang terbentuk memiliki struktur berbasis olivin dengan grup ruang ortorombik serta terjadi pergeseran puncak akibat penambahan vanadium. Hasil SEM menunjukan morfologi LiFePO4 yang teraglomerasi, meskipun berkurang seiring meningkatnya kadar vanadium. Hasil uji EIS menunjukan bahwa terjadi peningkatan konduktivitas dari 2.02x10-5 S/cm pada 0 menjadi 4.37x10-5 S/cm pada 5 vanadium. Hal yang sama juga terjadi dengan adanya karbon sintesis dari gula namun pelapisan karbon aktif dari bambu menghasilkan konduktivitas yang lebih baik. LiFePO4 synthesis process has been carried out by hydrothermal method followed by vanadium doping and bamboo activated carbon coating for lithium ion battery cathode. In the LiFePO4 synthesis process, precursor of LiOH, NH4H2PO4 and FeSO4.7H2O was measured according to stoichiometry with 2 1 1 molar ratio. The synthesis process is produced powder LiFePO4 pure light gray.The as synthesized LiFePO4 was then mixed with H4NO3V powder and activated carbon from bamboo as much as 4 wt. Then characterized by thermal analysis STA to determine sintering temperature. The STA results show that the transition temperature starts to occur at 639°C which is then used as sintering process. The sintering results were further characterized using X ray diffraction XRD , electron microscopy SEM , and impedance spectroscopy EIS. The results of characterization by XRD show that the LiFePO4 phase formed has an olivine based structure with orthorhombic groups and a peak shift due to the addition of vanadium. The SEM results show the agglomerated lithium morphology of LiFePO4, although it decreases with increasing levels of vanadium. The result of EIS test showed that there was an increase of conductivity from 2.02x10 5 S cm at 0 to 4.37x10 5 S cm in 5 vanadium. The same is true of the carbon synthesis of sugars but the activated carbon from bamboo as a coating produces better conductivity. |
 S68946-Subkhan Alfaruq .pdf :: Unduh
|
| No. Panggil : | S68946 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2017 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xiv, 53 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S68946 | 14-19-656932842 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20457203 |