Karakterisasi serbuk logam stainless steel hasil atomisasi gas dengan variasi tekanan gas untuk proses metal injection molding = Characterization of metal powder produced by gas atomization with the variation of gas pressure for metal injection molding application
Muhammad Haekal Sena Akbar;
Bambang Suharno, supervisor; Sugeng Supriadi, examiner; Deni Ferdian, examiner
([Publisher not identified]
, 2018)
|
|
ABSTRAK Metalurgi serbuk merupakan proses pembuatan serbuk dan benda jadi dari serbuk logam atau paduan logam dengan ukuran tertentu tanpa melalui proses peleburan. Perkembangan industri Powder Metallurgy P/M atau metalurgi serbuk di Asia sangat berkembang pesat jika dibandingkan dengan metalurgi ingot konvensional. Salah satu metode P/M yang paling tepat untuk menghasilkan benda-benda dengan tingkat kepresisian tinggi dalam jumlah yang besar ialah melalui metode Metal Injection Molding MIM. Namun, perkembangan penelitian di bidang metalurgi serbuk di Indonesia masih kurang, apalagi jika dibandingkan dengan pioneer perkembangan teknologi metalurgi serbuk di asia seperti Jepang, Cina, dan India. Tujuan dari penelitian ini adalah untuk memproduksi bahan baku dari metalurgi serbuk, yaitu serbuk logam, dengan metode atomisasi gas dan menggunakan alat atomisasi yang dikembangkan sendiri. Logam yang akan digunakan adalah Stainless Steel karena menjadi salah satu logam yang paling sering digunakan untuk proses MIM. Penelitian akan memvariasikan tekanan gas selama proses atomisasi dengan variasi tekanan 12 Bar, 10 Bar, dan 8 Bar. Hasil penelitian menunjukkan bahwa jumlah serbuk berukuran kecil akan semakin banyak seiring dengan meningkatnya tekanan gas selama proses atomisasi gas. Serbuk yang dihasilkan dari penelitian ini dengan menggunakan alat yang dikembangkan sendiri sudah memiliki ukuran. ABSTRACT Powder Metallurgy P M is a metal product makin process using metal or metal alloy powder as the raw material without smelting process. The development of P M industry in Asia have grown significantly, compared to conventional ingot process. Metal Injection Molding MIM is one of the most appropriate method in P M for producing products with high precision and high quantity. However, research and technology development of P M in Indonesia is still lacking, moreover if compared to research and technology development of P M in other Asia rsquo s leading country such as Japan, China, and India. This research rsquo s aim is to produce the raw material for P M, which is metal powder, using gas atomization and a self developed atomization device. The metal used in this research is Stainless Steel due to it rsquo s frequent utilization in MIM. This research will varying the gas pressure of the atomization process with the variation of 12 Bar, 10 Bar, and 8 Bar. The results shows that metal powder with smaller size will be produced more using the higher gas pressure. The self developed atomization device have successfully produced metal powder with the size. |
 Muhammad Haekal Sena Akbar.pdf :: Unduh
|
| No. Panggil : | S-Pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | [Place of publication not identified]: [Publisher not identified], 2018 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer (rdadontent) |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xiv, 93 pages : illustration ; appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-Pdf | 14-21-505293953 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20465956 |