Elektroda boron doped-diamond BDD termodifikasi emas Au telah berhasil dipreparasi dengan cara seeding diikuti elektrodeposisi larutan HAuCl4 pada permukaan elektroda. Teknik seeding berfungsi untuk membuat bibit benih inti emas pada permukaan elektroda BDD melalui adsorpsi fisik. Sedangkan elektrodeposisi dilakukan untuk menghomogenkan ukuran dan sebaran partikel emas di permukaan elektroda BDD. Partikel Au yang terdeposisi dipermukaan elektroda BDD dikarakterisasi menggunakan Scanning Electron Microscopy-Energy Dispersive Spectroscopy SEM-EDS dan X-Ray Photoelectron Spectroscopy XPS. Deteksi As3, As5, dan campuran As3 dan As5 dilakukan dengan teknik anodic stripping voltammetry ASV. Mula-mula dilakukan pre-treatment menggunakan NaBH4 untuk mereduksi As5 menjadi As3 untuk menurunkan potensial deposisi As3 karena deposisi As5 memerlukan potensial deposisi yang sangat negatif dan dapat menimbulkan evolusi gas hidrogen yang dapat mengganggu pengukuraan. Respon arus terhadap masing-masing larutan standar As3 dan As5 menunjukkan linearitas yang baik pada rentang konsentrasi 0,1-1 ppmdengan R2= 0,97598 untuk As3 dan range konsentrasi 0,048-0,48 ppm dengan R2= 0,98767 untuk As5 . Limit deteksi yang dihasilkan pada pengukuran As3 sebesar 0,1675 ppm, sedangkan As5 0,0574 ppm. Pengukuran pada campuran As3 dan As5 menunjukkan linearitas yang tinggi, mengindikasikan bahwa dimungkinkan untuk mengukur konsentrasi masing-masing As3 dan As5 dalam matriks campuran.
Boron doped diamond BDD electrode modified with gold particles Au has been successfully prepared by seeding followed by electrodeposition of HAuCl4 solutions at the electrode surface. The function of seeding method is to deposite gold seeds onto the electrode surface by physical adsorption. Whereas the electrodeposition was performed to homogenize the size and distribution of the particles at the BDD electrode surface. The deposited gold particles on BDD surface were characterized using Scanning Electron Microscopy Energy Dispersive Spectroscopy SEM EDS and X Ray Photoelectron Spectroscopy XPS . Detection of As3 , As5 , and mixture solutions of As3 and As5 using anodic stripping voltammetry. Initially, pretreatment used NaBH4 was performed to reduce As5 to As3 , therefore the deposition potential can be decreased. It is known that As5 required high negative deposition potential, which can cause hydrogen gas evolution which can affecting the measurements. Good linear responses for each solution were observed in range consentration of 0,1 1 ppm for As3 R2 0,97598 and range concentration of 0,048 0,48 ppm for As5 R2 0,98767. Limit of detections of 0,1675 ppm and 0,0574 ppm can be achieved for As3 and As5 , respectively. Measurements of mixture solutions of As3 and As5 showed high linearity, indicating that detection of each species of As3 and As5 can be performed in mixture As3 and As5. |
S-Dian Tri Lestarini.pdf :: Unduh