Pengaruh anil terhadap sifat struktur dan sifat listrik double perovskite La2FeTiO6 dipreparasi dengan metode sol-gel = Effect of annealing on structural and electrical properties of double perovskite La2FeTiO6 prepared by sol-gel method
Riza Enu Annisa Utami;
Djoko Triyono, supervisor; Dede Djuhana, examiner; Muhammad Aziz Majidi, examiner; Muhammad Aziz Majidi, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2017)
|
|
Telah dilakukan penelitian sifat struktur dan sifat listik material double perovskite La2FeTiO6 yang di preparasi dengan metode sol-gel. Hasil karakterisasi XRD sampel bubuk hasil kalsinasi 9000C selama 6 jam menunjukkan La2FeTiO6 memiliki struktur kristal orthorhombik dengan space grup Pnma, masih terdapat fase kedua berupa senyawa nitrat. Sampel disinter pada suhu 13000C untuk mendapatkan bentuk bulk yang keras dan tidak mudah pecah. Hasil karakterisasi XRD sampel bulk hasil sintering menunjukkan telah diperoleh fase tunggal dengan crystallite size 24.1nm. Sampel dianil pada suhu 11000C selama 4 jam untuk memperbaiki mikrostruktur material sehingga dapat menghasilkan sifat listrik yang lebih baik. Hasil karakterisasi XRD menunjukkan sampel bulk hasil anil memiliki fase tunggal dengan intensitas peak yang meningkat dan crystallite size menurun 21.7nm , menunjukan terbentuknya kristalisasi yang baik. Hasil karakterisasi SEM menunjukan La2FeTiO6 hasil sinter dan hasil anil memiliki bentuk butiran yang seragam dengan ukuran yang berbeda-beda. Rata-rata grainsize 247nm untuk La2FeTiO6 hasil sinter dan 137nm untuk La2FeTiO6 hasil anil. Hasil EDS menunjukan tidak terlihat adanya kemunculan elemen lain yang mengindikasikan fase sekunder pada sampel sinter dan anil. Sifat listrik material dianalisis dengan impedansi spectroskopi. Hasil yang diperoleh menunjukan La2FeTiO6 hasil anil memiliki nilai konstanta dielektrik dan konduktivitas lebih tinggi dibandingkan dengan hasil sinter. The structure and electrical properties of double perovskite La2FeTiO6 by sol gel method have been investigated. XRD characterization of calcined sample powder at 9000C for 6 hours showed La2FeTiO6 has orthorhombic crystal structure with space group Pnma, there is still impurities of nitrate compound. Samples were sintered at 13000C to obtain samples in bulk form which were hard and not easily broken. XRD characterization of the sintered bulk sample showed a single phase with crystallite size 24.1nm. Samples were annealed at 11000C for 4 hours to improve microstructure of material so can produce a better electrical properties. XRD characterization show the annealed bulk have increased peak intensity and decreased crystallite size 21.7nm . Indicating that a good crystallization was form. SEM characterization shows, double perovskite La2FeTiO6 sinter and anneal well separated with different grain size . Grain size average of La2FeTiO6 sintered and annealed are 247 nm and 137 nm respectively. EDS results show no visible presence of other elements that indicate secondary phase in sinter and anneal samples. Electrical properties materials are analyzed by impedance spectroscopy. The result shows that La2FeTiO6 annealed has dielectric constant and conductivity value which is superior than La2FeTiO6 sintered |
 T49799-Riza Enu Annisa Utami .pdf :: Unduh
|
| No. Panggil : | T49799 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2017 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | x, 41 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| T49799 | 15-19-244587185 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20467180 |