Studi pengaruh variasi konsentrasi NaCl dan inhibitor ammonium molibdat terhadap serangan korosi sumuran pada material baja tahan karat duplex 2205 dengan metode polarisasi dan EIS = The influence of addition of nacl and ammonium molybdate inhibitor on pitting corrosion on duplex stainless steels 2205 using cylic polarization and EIS method

Apriyan Tri Kusuma; Rini Riastuti, supervisor; Mochamad Chalid, examiner; Sutopo, examiner (Fakultas Teknik Universitas Indonesia, 2018)

 Abstrak

Ketahanan Korosi Sumuran pada 2205 Duplex Stainless Steels, ditentukan dengan uji elektrokimia dengan kadar 1 berat, 2 berat, 3,5 berat, 4 berat, 5 berat larutan NaCl dan 100ppm, 150ppm, 200ppm, 250ppm amonium molibdat pada 3,5 berat larutan NaCl. Hasilnya menunjukkan bahwa Baja tahan karat Duplex pada Larutan NaCl 3,5 berat memiliki ketahanan korosi yang paling rendah, diikuti oleh 4 berat, 5 berat, 2 berat, 1 berat. Sedangkan 100ppm, 150ppm, 200ppm, 250ppm amonium molibdat ditambahkan ke 3,5 berat larutan NaCl dan ditunjukkan bahwa penambahan amonium molibdat dapat meningkatkan Ketahanan pitting pada baja tahan karat Duplex 2205 pada larutan NaCl 3,5 berat.

Pitting Corrosion resistance of 2205 Duplex Stainless Steels, determined by electrochemical test at 1 wt, 2 wt, 3.5 wt, 4 wt, 5 wt of NaCl Solution and 100ppm, 150ppm, 200ppm and 250ppm of amonium molybdate at 3.5 wt of NaCl Solution has been investigated. The result show that Duplex Stainless Steels at 3.5 wt NaCl Solution had the most suspectible to pitting, followed by 4 wt, 5 wt, 2 wt, 1 wt. The 100ppm, 150ppm, 200ppm and 250ppm of amonium molybdate added to 3.5 wt NaCl Solution and its was shown that the addition of ammonium molybdate can increase pitting potential and reduce suspectibility on pitting of 2205 Duplex Stainless Steels at 3.5 wt NaCl solution.

 File Digital: 1

Shelf
 T49074-Apriyan Tri Kusuma .pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : T49074
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2018
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiv, 88 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
T49074 15-19-223412411 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20467326