Sintesis komposit karbon aktif-Ag/TiO2 berbasis limbah tandan kosong kelapa sawit untuk purifikasi udara pada ruang medis = Synthesis of oil palm empty fruit bunch waste based activated carbon-Ag/TiO2 composite for air purification in medical room
Dimas Nurwansyah;
Slamet, supervisor; Eny Kusrini, examiner; Bambang Heru Susanto, examiner
(Fakultas Teknik Universitas Indonesia, 2018)
|
|
Pemanfaatan limbah tandan kosong kelapa sawit untuk sintesis komposit karbon aktif-Ag/TiO2 untuk purifikasi udara pada ruang medis telah diteliti. Tujuan dari penelitian ini adalah untuk memperoleh komposisi terbaik dari komposit karbon aktif-Ag/TiO2 dalam memurnikan udara ruang medis. Karbon aktif disintesis dari tandan kosong kelapa sawit melalui dua tahapan, karbonisasi dan aktivasi kimia dengan ZnCl2. Kemudian, permukaan karbon aktif diberi perlakuan dengan TEOS untuk memastikan terbentuknya komposit. Komposit Ag/TiO2 disintesis dengan metode photo-assisted deposition PAD. Kinerja Ag/TiO2 diuji untuk mendisinfeksi bakteri E. coli. Sintesis karbon aktif-Ag/TiO2 dilakukan dengan variasi loading karbon aktif sebesar 2, 5 dan 10. Kemampuan karbon aktif-Ag/TiO2 dalam mendegradasi formaldehida juga diuji. Hasil karakterisasi BET menunjukkan karbon aktif yang terbentuk memiliki luas permukaan yang tinggi SBET = 657-752 m2/g. Karakterisasi EDX dari karbon aktif menunjukkan kandungan unsur karbon pada karbon aktif mencapai 90. Katalis 3 Ag/TiO2 memiliki kemampuan terbaik dalam mendisinfeksi bakteri E. coli hingga 0 CFU/ml. Kemampuan degradasi fotokatalisis terbaik dari formaldehida dimiliki oleh komposit dengan perbandingan massa KA : Ag : TiO2 sebesar 1 : 1,4 : 47,6. Formaldehida mampu terdegradasi hingga konsentrasi mencapai standar kualitas udara dalam ruang medis di Indonesia sebesar 0,1 ppm. Efek sinergis dari masing-masing penyusun komposit terhadap kinerja komposit juga didiskusikan. The utilization of waste of palm oil empty bunches for the synthesis of activated carbon composite Ag TiO2 for air purification in medical space has been investigated. The purpose of this study was to obtain the best composition of the activated carbon composite Ag TiO2 in purifying the medical room air. Activated carbon is synthesized from oil palm empty bunches through two stages, carbonization and chemical activation with ZnCl2. Then, the surface of the activated carbon was treated with TEOS to ensure the formation of the composite. Composite Ag TiO2 is synthesized by photo assisted deposition method PAD. Performance of Ag TiO2 was tested to disinfect E. coli bacteria. The synthesis of activated carbon Ag TiO2 was carried out with variations of activated carbon loading of 2, 5 and 10. The ability of activated carbon Ag TiO2 in degrading formaldehyde was also tested under UV radiation. The BET characterization results show that the activated carbon formed has a high surface area SBET 657 752 m2 g. Characterization of EDX from activated carbon showed carbon content in activated carbon reach 90. The 3 Ag TiO2 catalyst has the best ability to disinfect E. coli bacteria up to 0 CFU ml for 2 hours. The best photocatalytic degradation capability of formaldehyde is owned by 2 activated carbon 3 Ag TiO2 or mass ratio of AC Ag TiO2 is 1 1.4 47.6. Formaldehyde is able to be degraded until concentration reaches the indoor air quality standard in Indonesia at 0.1 ppm. The synergetic effect of each component in the composite will also be dicussed. |
 S-pdf-Dimas Nurwansyah.pdf :: Unduh
|
| No. Panggil : | S-Pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2018 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xiii, 62 pages : illustration ; appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-Pdf | 14-20-843253133 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20473305 |