Karakterisasi dan pembuatan metakaolin hasil rekayasa proses kalsinasi kaolin Pulau Bangka = Characterization and production of metakaolin result of engineered calcination process using kaolin from Bangka Island
Banjarnahor, Irwin Marlundu;
Sotya Astutiningsih, supervisor; Akhmad Herman Yuwono, examiner; Sri Harjanto, examiner; Hutabarat, Imelda Eva, examiner
(Fakultas Teknik Universitas Indonesia, 2018)
|
|
Metakaolin telah berhasil dibuat menggunakan kaolin Pulau Bangka dengan proses kalsinasi. Pada penelitian ini proses kalsinasi menggunakan lima variabel temperatur: 600, 650, 700, 750, dan 800°C selama 4 jam. Pada penelitian ini, kaolin juga diberikan perlakuan mekanik berupa milling untuk mempelajari pengaruh perlakuan milling terhadap produk hasil kalsinasi. Kaolin di-milling menggunakan planetary ball mill selama 15 menit dengan kecepatan milling sebesar 20rad/min dan kemudian dikalsinasi dengan masing-masing variabel temperatur. Sebagai material pembanding, metakaolin komersial dengan produk dagang MetaStar digunakan untuk dibandingkan karakteristiknya dengan metakaolin yang dihasilkan pada setiap temperatur. Hasil perlakuan milling kaolin, beserta kaolin dan MetaStar dikarakterisasi distribusi ukuran partikelnya menggunakan instrumen Particle Size Distribution. Kemudian, setiap metakaolin dan juga MetaStar akan dikarakterisasi menggunakan instrumen X-Ray Diffraction XRD dan Scanning Electron Microscope SEM . Pengujian Simultaneous Thermal Analysis STA juga dilakukan untuk mempelajari perilaku pemanasan kaolin dan kaolin dengan perlakuan milling. Hasil karakterisasi XRD menunjukkan kemiripan antara metakaolin Bangka dengan MetaStar, pengecualian untuk metakaolin MK800-MT. Hasil pengujian STA menunjukkan adanya pergeseran temperatur dimana kaolin mengalami dehidroksilasi dan rekonstruksi setelah kaolin diberi perlakuan milling. Dan kemudian, hasil pengujian SEM menunjukkan keberadaan struktur kaolinite berbentuk lapisan lamelar-laminate. Dapat disimpulkan bahwa tidak ada perubahan struktur yang terlihat setelah kaolin dikalsinasi. Metakaolin has been successfully made using Pulau Bangka rsquo s kaolin through calcination process. In this study, the calcination process used five temperature variables 600, 650, 700, 750, and 800°C for 4 hours. In this study, kaolin is subjected to mechanical treatment to study the effect of the treatment on the product of calcination. Kaolin is milled using a planetary ball mill for 15 minutes at a milling speed of 20rad min and then calcined with each temperature variable. As a comparison material, commercial metakaolin MetaStar products is used to compare its characteristic to the metakaolin produced at each temperature. The results of milling treatment, along with kaolin and MetaStar is characterized using the particle size distribution instrument to determine the particle size. Then, each metakaolin and MetaStar will be characterized using X Ray Diffraction XRD and Scanning Electron Microscope SEM instruments. Simultaneous Thermal Analysis STA was also conducted to study the heating behavior of kaolin and kaolin after milling treatment. The results of XRD characterization show similarities between metakaolin Bangka and MetaStar, except to MK800 MT metakaolin. The STA test results showed a temperature shift in which the kaolin was dehydroxylated and reconstructed after kaolin was treated with milling. And then, the SEM test results show the existence of kaolinite structures in the form of lamellar laminate layers. It can be concluded that there is no structural changes happened after the kaolin is calcined. |
 Irwin Marlundu Banjarnahor.pdf :: Unduh
|
| No. Panggil : | S-Pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2018 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer recource |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xiv, 52 pages : illustration ; appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-Pdf | 14-20-704644499 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20473909 |