Deteksi arsen dengan teknik anodic stripping voltammetry menggunakan boron-doped diamond termodifikasi platina = Arsenic detection with anodic stripping voltammetry technique using boron doped diamond modified platinum
Sitorus, Paulus Pardamean Rinaldo;
Ivandini Tribidasari Anggraningrum, supervisor; Asep Saefulmillah, supervisor; Jarnuzi Gunlazuardi, examiner; Iman Abdullah, examiner; Munawar Khalil, examiner; Endang Asijati Widijaningsih Ichsan, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2018)
|
Preparasi elektroda boron-doped diamond (BDD) termodifikasi platina (Pt) berhasil dilakukan menggunakan teknik wet seeding yang diikut oleh elektrodeposisi. Pt yang terdeposisi pada permukaan BDD dikarakterisasi menggunakan Scanning Electron Microscopy-Energy Dispersive Spectroscopy (SEM-EDS) yang menunjukkan %Pt pada permukaan BDD sebesar 1.54 %. Elektroda ini digunakan untuk sensor As3+ dan As5+ menggunakan teknik Anodic Stripping Voltammetry (ASV). Hasil deteksi As3+ yang diperoleh pada kondisi optimum pada potensial deposisi -500 mV, waktu deposisi 150 detik dan laju deteksi 200 mV/s menunjukkan bahwa linieritas tinggi (R2 = 0.9797) pada rentang konsentrasi 0 sampai 100 ppb dengan limit deteksi (LOD) sebesar 16.50 ppb, sementara hasil deteksi As5+ dengan pre-treatment menggunakan NaBH4 0.1 M pada kondisi optimum yang sama menunjukkan linieritas yang tinggi (R2 = 0.9903) pada rentang konsentrasi 0 sampai 100 ppb memiliki linearitas yang tinggi dengan LOD sebesar 8.19 ppb. Boron-doped diamond electrode modified by platinum was successfully prepared using wet seeding technique followed by electrodeposition. Pt deposited on the surface of BDD characterized using Scanning Electron Microscopy-Energy Dispersive Spectroscopy (SEM-EDS) which shows %Pt on BDD surface are 1.54%.These modified electrode are used for As3+ and As5+ sensors using the Anodic Stripping Voltammetry (ASV) technique. As3+ and As5+ detection results obtained using the same deposition potential of -500 mV, deposition time of 150 s and detection rate of 200 mV/s, with addition of 0.1 M NaBH4 for As5+ solution, shows that the calibration in the concentration range 0 to 100 ppb has high linearity (R2 = 0.9797 and 0.9903, respectively) with LOD at 16.50 and 8.19 ppb, respectively. |
![]()
|
No. Panggil : | T51884 |
Entri utama-Nama orang : | |
Entri tambahan-Nama orang : | |
Subjek : | |
Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2018 |
Program Studi : |
Bahasa : | ind |
Sumber Pengatalogan : | LibUI ind rda |
Tipe Konten : | text |
Tipe Media : | unmediated ; computer |
Tipe Carrier : | volume ; online resource |
Deskripsi Fisik : | xvi, 92 pages : illustration ; 28 cm + appendix |
Naskah Ringkas : | |
Lembaga Pemilik : | Universitas Indonesia |
Lokasi : | Perpustakaan UI, Lantai 3 |
No. Panggil | No. Barkod | Ketersediaan |
---|---|---|
T51884 | 15-20-213468476 | TERSEDIA |
Ulasan: |
Tidak ada ulasan pada koleksi ini: 20480911 |