Studi sifat struktur dan sifat listrik material perovskite La1-xPbx Fe0.5Ti0.5O3 (x = 0.1, 0.2, 0.3) = Study of structure and electrical properties of material perovskite La1-xPbx Fe0.5Ti0.5O3 (x = 0.1, 0.2, 0.3)
Yusuf Supriadi;
Djoko Triyono, supervisor; Efta Yudiarsah, examiner; Dede Djuhana, examiner; Muhammad Aziz Majidi, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2019)
|
|
Material La1-xPbxFe0.5Ti0.5O3 (x = 0.1, 0.2, 0.3) telah disintesis dengan menggunakan metode sol-gel. Hasil karakterisasi XRD menunjukan material memiliki struktur orthorhombik space group Pnma dan diperoleh fase tunggal untuk konsentrasi x = 0.2 dan x = 0.3 Hasil karakterisasi XRF mengkonfirmasi bahwa konsentrasi unsur-unsur penyusun material La1-xPbxFe0.5Ti0.5O3 (x = 0.1, 0.2, 0.3) sesuai dengan perhitungan stoikiometri yang diharapkan. Hasil pengukuran SEM menunjukan distribusi ukuran grain pada permukaan sampel Bulk mengalami peningkatan seiring dengan kenaikan konsentrasi Pb. Karakterisasi sifat listrik dilakukan pada material La1-xPbxFe0.5Ti0.5O3 dengan konsentrasi x = 0.2 dan x = 0.3. Plot Nyquist menunjukan semicircle yang semakin mengecil seiring dengan kenaikan temperatur yang menunjukan fenomena negative temperature coefficient resistance (NTCR). Konstanta dielektrik dan energi aktivasi mengalami peningkatan seiring dengan peningkatan konsentrasi Pb. Material La1-xPbxFe0.5Ti0.5O3 (x = 0.1, 0.2, 0.3) has been synthesized using the sol-gel method. XRD characterization results show that the material has an orthorhombic space group Pnma structure. The results of XRF characterization confirm that the concentration of La1-xPbxFe0.5Ti0.5O3 material (x = 0.1, 0.2, 0.3) was in expected stoichiometric calculation. The SEM measurement results show the grain size distribution of Bulk materials increas along with the increasing Pb concentration. Characterization of electrical properties was carried out on La1-xPbxFe0.5Ti0.5O3 material with concentrations of x = 0.2 and x = 0.3. Nyquist plots show a semicircle that decreases with increasing temperature which shows the phenomenon of negative temperature coefficient resistance (NTCR). The dielectric constant and activation energy increase with increasing Pb concentration. |
 T52295-Yusup Supriyadi.pdf :: Unduh
|
| No. Panggil : | T52295 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2019 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xii, 39 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| T52295 | 15-20-794951175 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20482500 |