Sintesis nanokomposit SiO2/NiMoO4 menggunakan ekstrak daun bandotan (Ageratum conyzoides L.) dan aktivitas Katalis untuk Reduksi 2,4,6-trinitrofenol = Synthesis of SiO2/NiMoO4 Nanocomposite using Bandotan (Ageratum conyzoides L.) Leaf Extracts and Their Activity as Catalyst in Reduction of 2,4,6-trinitrophenol
Miessya Wardani;
Yoki Yulizar, supervisor; Iman Abdullah, supervisor; Jarnuzi Gunlazuardi, examiner; Munawar Khalil, examiner; Widayanti Wibowo, examiner; Agustino Zulys, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2019)
|
|
Nanokomposit SiO2/NiMoO4 telah berhasil disintesis menggunakan fraksi air ekstrak daun bandotan (Ageratum conyzoides L.) sebagai sumber basa dan capping agent dalam proses sintesis. Keberhasilan sintesis nanomaterial dikonfirmasi dari hasil karakterisasi yang dilakukan. Spektra FTIR menunjukkan adanya vibrasi khas logam dengan oksigen pada rentang bilangan gelombang 1000-400 cm-1. Karakterisasi XRD menunjukkan bahwa terbentuknya kristalin nanopartikel SiO2, nanopartikel NiO dengan struktur kubik, MoO3 dengan struktur ortorombik, NiMoO4 dengan struktur monoklinik, dan SiO2/NiMoO4 memiliki pola difraksi 2θ gabungan dari penyusunnya. Komposisi logam Ni dan Mo pada nanokomposit SiO2/NiMoO4 dikarakterisasi menggunakan AAS didapatkan masing-masing sebesar 19,36% w/w dan 22,36% w/w. Uji aktivitas katalitik nanokomposit SiO2/NiMoO4 dilakukan sebagai katalis reduksi untuk senyawa 2,4,6-trinitrofenol dengan NaBH4. Kondisi optimum nanokomposit untuk mereduksi senyawa nitro didapatkan pada massa katalis 3 mg dengan konsentrasi 2,4,6-trinitrofenol 5x10-5 M dan NaBH4 0,1 M. Hasil studi kinetika menunjukkan bahwa reaksi reduksi mengikuti hukum laju orde pertama dengan nilai tetapan laju reaksi reduksi sebesar 0,01 menit. Nanokomposit SiO2/NiMoO4 nanocomposite was successfully synthesized using water fraction of bandotan (Ageratum conyzoides L.) leaf extract as a base source and capping agent in the synthesis process. The success of nanomaterial synthesis was confirmed from the results of the characterization being carried out. FTIR spectra showed the presence of a typical metal vibration with oxygen in the wave number range 1000-400 cm-1. XRD characterization showed that SiO2 nanoparticles, NiO nanoparticles crystalized on cubic structure, MoO3 on orthorhombic structure, NiMoO4 on monoclinic structure. The XRD of SiO2/NiMoO4 nanocomposite showed a 2θ diffraction pattern from their constituents. The composition of Ni and Mo metals on SiO2/NiMoO4 characterized using AAS was obtained at 19.36% w/w and 22.36% w/w, respectively. The catalyst SiO2/NiMoO4 nanocomposite was used as the reduction catalyst for 2,4,6-trinitrophenol compounds with NaBH4. The optimum condition of nanocomposite to reduce nitro compounds was obtained at a weight of 3 mg with 2,4,6- trinitrophenol concentration at 5x10-5 M and NaBH4 0,1 M. The results of the kinetic study show that the reduction reaction follows the first order rate law with the reduction reaction rate constant of 0.01 minutes-1. |
 T51684-Miessya Wardani.pdf :: Unduh
|
| No. Panggil : | T51684 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2019 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xv, 106 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| T51684 | 15-21-876020649 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20486331 |