Sifat optik dan listrik material lanthanum orthoferrite di substitusi Mg pada Site-La (La1-xMgxFeO3) yang di sintesis dengan metode sol-gel = Optical and electrical properties of Lanthanum Orthoferrite substituted Mg on La-site (La1-xMgxFeO3) with sol-gel method

Rianty Warto Utami; Djoko Triyono, supervisor; Dedi Suyanto, examiner; Cuk Imawan, examiner; Muhammad Aziz Majidi, examiner ([Publisher not identified] , 2019)

 Abstrak

Substitusi Mg pada site-La material LaFeO3 (La1-xMgxFeO3, dengan x=0.0, 0.1, 0.2 dan 0.3) telah dilakukan dengan metode sintesis sol-gel. Sifat struktur material perovskite La1-xMgxFeO3 dikarakterisasi menggunakan XRD, XRF, BET, SEM dan EDX. Analisis XRD material La1-xMgxFeO3 menunjukkan struktur Orthorhombic dengan space group Pnma. Terjadi penurunan crystallite size seiring dengan meningkatnya konsentrasi Mg. Analisis BET menunjukkan terjadinya peningkatan surface area seiring penambahan konsentrasi Mg. Hasil SEM menunjukkan bahwa ukuran grain terlihat semakin menurun dan terjadi aglomerasi. XRF dan EDX mengkonfirmasi adanya unsur La, Mg, Fe dan O pada material perovskite La1-xMgxFeO3. Sifat optik dikarakterisasi dengan menggunakan FTIR, Raman spectroscopy dan UV-Vis. FTIR mengkonfirmasi adanya stretching vibration La/Mg−O, Fe−O dan bending vibration Fe−O−Fe. Hasil karakterisasi UV-Vis menunjukkan penurunan nilai energi band gap dengan rentang 2.14–2.05 eV. Sifat listrik material diuji menggunakan RLC-meter dengan metode Impedance Spectroscopy (IS) pada temperatur ruang dan temperatur tinggi (30oC-200oC).


Mg substitution on La-site at LaFeO3 (La1-xMgxFeO3, with x=0.0, 0.1, 0.2, and 0.3) has been done by sol-gel method. The structural properties of La1-xMgxFeO3 perovskite material were characterized using XRD, XRF, BET, SEM and EDX. XRD analysis of La1-xMgxFeO3 material shows the Orthorhombic structure with the Pnma space group. There was a decrease in crystallite size with increasing Mg concentration. BET analysis shows an increased surface area with the increase of Mg concentration. SEM analysis shows that the grain size appears to decrease and agglomeration occurs. XRF and EDX confirmed the presence of La, Mg, Fe and O element in La1-xMgxFeO3 perovskite material. Optical properties were characterized using FTIR, Raman spectroscopy and UV-Vis. FTIR confirmed the presence of stretching vibration of La/Mg−O, Fe−O and bending vibration of Fe−O−Fe. The results of UV-Vis characterization showed a decrease in the band gap energy value with a range of 2.14–2.05 eV. The electrical properties were characterized by RLC-meters using Impedance Spectroscopy (IS) method at room temperature and high temperatures (300C-2000C).

 File Digital: 1

Shelf
 T54019-Rianty Warto Utami.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : T54019
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2019
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiii, 70 pages : illustrations ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
T54019 15-21-037723969 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20492694