Rekayasa Zeolit Alam Bayah dengan Penambahan Larutan FeCl3.6H2O dan proses Ultrasonik sebagai kandidat adsorben gas H2S = Modification of Bayah Natural Zeolite with FeCl3.6H2O Solution and Ultrasonic Process as H2S gas Adsorbent Candidate
Thomas Agus Bayu Prasetyo;
Bambang Soegijono, supervisor; Budhy Kurniawan, examiner; Djonaedi Saleh, examiner; Nurlely, examiner; Yusmaniar, examiner; Musfirah Cahya Fajrah Toana, examiner
(Universitas Indonesia, 2019)
|
|
Rekayasa terhadap material zeolit alam Bayah untuk memperbaiki karakteristik material yang lebih baik dan seragam telah dilakukan dengan menambahkan FeCl3.6H2O dan proses perlakuan ultrasonik dengan variasi waktu untuk melihat perubahan yang terjadi pada zeolit. Karakterisasi dengan XRD memperlihatkan puncak baru difraksi, hasil konfirmasi dengan EDS menunjukkan perubahan elemen Fe sebesar 215.77%wt. Distribusi ukuran partikel dengan metode NIBS memperlihatkan hubungan antara waktu proses ultrasonik terhadap ukuran partikel, semakin lama proses ultrasonik akan berdampak pada ukuran partikel, selain itu pada pengujian BET juga memperlihatkan adanya perbaikan luas permukaan sebesar 30.80%, volume pori-pori 62.51% dan ukuran pori-pori 5.50%. Perlakuan ultrasonik terhadap zeolit juga memperlihatkan pergeseran bidang kristal (020) dan (200) pada intensitas difraksi tertinggi XRD. Spektrum infra merah zeolit yang di ultrasonik juga memperlihatkan munculnya puncak kedua hydroxil, peregangan O-H pada 3.800-3.400 cm-1 menunjukkan bahwa absorbsi ganda yang muncul sangat bermanfaat sebagai bahan baku absorbsi, hasil analisa setelah proses adsorbsi H2S juga memperlihatkan pergeseran puncak adsorbsi sinar infra merah dan munculnya ikatan S=O. Kinerja zeolit Bayah dengan penambahan FeCl3.6H2O dan perlakuan ultrasonik, memperlihatkan kenaikan adsorbsi gas H2S sebesar 70%wt sampai 117%wt lebih tinggi dibandingkan tanpa penambahan FeCl3.6H2O dan perlakuan ultrasonik. Kinerja adsorbsi gas H2S hasil riset zeolit Bayah juga menunjukkan kinerja adsorbsi maksimum 150%wt lebih tinggi dari produk komersial PURAFIL® PURACARB MEDIA. Modification of Bayah natural zeolite to improve material characteristics and uniformly has been done by adding FeCl3.6H2O and ultrasonic treatment process with a time variation to see changes that occur in zeolites. XRD characterization showed a new diffraction peak, the confirmation results with EDS showed changes in Fe elements of 215.77% wt. Particle size distribution using the NIBS method shows the relationship between ultrasonic processing duration to particle size, the longer the ultrasonic process will have an impact on particle size. BET testing also shows an improvement in surface area of 30.80%, pore volume 62.51% and pore size 5.50%. The ultrasonic treatment of zeolite also shows a shift in the crystalline plane (020) and (200) at the highest diffraction intensity of XRD. Infrared spectrum in the ultrasonic process also shows the emergence of a second hydroxil peak, OH stretching at 3,800-3,400 cm-1 shows that the emerging double absorption is very useful as a raw material for absorption and the appearance of the S=O bond. Bayah zeolite performance with the addition of FeCl3.6H2O and ultrasonic treatment, showed an increase in H2S gas adsorption of 70% wt to 117% wt higher than without the addition of FeCl3.6H2O and ultrasonic treatment. The performance of H2S gas adsorption from the Bayah zeolite research also shows a maximum adsorption performance of 150% wt higher than the PURAFIL® PURACARB MEDIA commercial product. |
 D2641-Thomas Agus Bayu Prasetyo.pdf :: Unduh
|
| No. Panggil : | D2641 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Universitas Indonesia, 2019 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resources |
| Deskripsi Fisik : | xiv, 102 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| D2641 | 15-20-416421877 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20493927 |