Pengujian efisiensi enkapsulasi dan disolusi secara in vitro mikrokapsul captopril yang tersalut polipaduan poli(D-asam laktat) dan polikaprolakton = In vitro testing of encapsulation and dissolution efficiency of captopril microcapsule coated by polyblend poly(D-lactic acid) and polycaprolactone
Imam Fachrudin;
Emil Budianto, supervisor; Noverra Mardhatillah Nizardo, examiner; Sri Handayani, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2019)
|
|
Dalam penelitian ini, dilakukan pembuatan mikrokapsul sebagai sistem penghantar obat terkontrol dari captopril yang tersalut oleh polipaduan poli(D-asam laktat) dan polikaprolakton dengan menggunakan surfaktan campuran Tween 80-Span 80 melalui metode penguapan pelarut. Berdasarkan optimasi yang dilakukan, didapatkan konsentrasi optimum surfaktan campuran berada pada konsentrasi 0,0741 M yang menghasilkan persen efisiensi enkapsulasi sebesar 28,245% dengan ukuran mikrokapsul sebesar 0,482 µm. Setelah didapatkan konsentrasi optimum dari surfaktan, dilakukan optimasi perbandingan komposisi polipaduan (PDLA:PCL). Komposisi optimum untuk menghasilkan persen enkapsulasi yang terbaik berada pada komposisi 2:8 (% b/b) dengan persen efisiensi enkapsulasi sebesar 24,0983%. Uji disolusi dilakukan pada masing-masing komposisi dan diperoleh pelepasan obat terbaik pada perbandingan komposisi 4:6 (% b/b) dengan persen pelepasan sebesar 100%. Hasil karakterisasi FTIR menunjukan bahwa interaksi yang terjadi baik antara polimer dengan polimer, maupun polimer dengan obat adalah interaksi fisika berupa ikatan hidrogen, gaya dipol-dipol, dan gaya Van Der Waals. In this study, captopril drug delivery system was made from microcapsules coated by poly (D-lactic acid) and polycaprolactone using a mixture of Tween 80 and Span 80 surfactants through solvent evaporation method. Based on the optimization result, the optimum mixture surfactant concentration was 0.0741 M, resulting in a percent encapsulation efficiency of 28.245% with a microcapsule size of 0.482 µm. After obtaining the optimum surfactant concentration, optimization of the ratio of polyblend composition (PDLA: PCL) was carried out. The optimum composition that obtained to produce the best percent encapsulation was 24.0983% with a composition ratio of 2:8 (% w/w). Dissolution test was carried out for each composition and the best release at composition ratio of 4: 6 (% w/w) with 100% release percentage. The results of FTIR characterization shows that the interactions that occur between polymers and polymers, and polymers with drugs are physical interactions such as hydrogen bonds, dipole-dipole forces, and Van Der Waals forces. |
 S-Pdf Imam Fachrudin.pdf :: Unduh
|
| No. Panggil : | S-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2019 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xiv, 60 pages : illustration ; appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-pdf | 14-21-002596690 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20494812 |