Studi Pengaruh Variasi Molar TiO2 dan Mn3O4 terhadap Karakteristik dan Aktivitas Fotokatalitik Nanokomposit Ag/TiO2/Mn3O4 dengan Methylene Blue Sebagai Model Polutan = Study of The Influence of TiO2 And Mn3O4 Molar Ratio to The Characteristic and Photocatalytic Activity of Ag/TiO2/Mn3O4 Nanocomposites with Methylene Blue as The Model of Organic Pollutant
Indrianita Lionadi;
Rosari Saleh, supervisor; Djoko Triono, examiner; Lusitra Munisa, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020)
|
|
Nanokomposit Perak, Titanium dioksida, dan Mangan (II,III) oksida (Ag/TiO2/Mn3O4) dengan berbagai rasio molar telah disintesis menggunakan metode hidrotermal. Pengukuran difraksi sinar-X (XRD) mengkonfirmasi struktur nanokomposit Ag/TiO2/Mn3O4 yang terdiri dari struktur kubik Ag, TiO2 anatase, dan Mn3O4 tetragonal. Rasio komposisi unsur nanokomposit Ag/TiO2/Mn3O4 diselidiki dengan fluoresensi sinar-X (XRF). Efek sinergis Ag, TiO2 dan Mn3O4 dapat meningkatkan efisiensi nanokomposit sebagai fotokatalis. Peningkatan efisiensi ditunjukkan dengan melebarnya rentang absorbansi pada hasil pengukuran UV-Vis Diffuse Reflectance. Pengukuran adsorpsi-desorpsi nitrogen menunjukkan bahwa penambahan geraham TiO2 mengakibatkan penurunan luas permukaan spesifik nanokomposit Ag/TiO2/Mn3O4, sedangkan hasil sebaliknya diberikan dengan penambahan geraham Mn3O4. Pada uji fotokatalitik, hasil terbaik ditunjukkan oleh nanokomposit Ag/TiO2/Mn3O4 dengan dominasi Mn3O4 untuk radiasi UV dan cahaya tampak. Pada kondisi optimum, nanokomposit Ag/TiO2/Mn3O4 mampu mendegradasi metilen biru hingga 91% dengan penyinaran selama 2 jam. Uji scavenger mengidentifikasi lubang sebagai spesies yang berkontribusi paling besar pada proses fotokatalitik ini. Uji reusabilitas dan stabilitas pada nanokomposit Ag/TiO2/Mn3O4 menunjukkan hasil positif. Silver, Titanium dioxide, and Manganese (II,III) oxide (Ag/TiO2/Mn3O4) nanocomposites with various molar ratios have been synthesized using the hydrothermal method. X-ray diffraction (XRD) measurements confirmed the structure of the Ag/TiO2/Mn3O4 nanocomposite consisting of a cubic structure of Ag, TiO2 anatase, and tetragonal Mn3O4. The elemental composition ratio of Ag/TiO2/Mn3O4 nanocomposite was investigated by X-ray fluorescence (XRF). The synergistic effect of Ag, TiO2 and Mn3O4 can increase the efficiency of nanocomposites as photocatalysts. The increase in efficiency is indicated by the widening of the absorbance range on the measurement results of UV-Vis Diffuse Reflectance. The nitrogen adsorption-desorption measurements showed that the addition of TiO2 molars resulted in a decrease in the specific surface area of the Ag/TiO2/Mn3O4 nanocomposite, while the opposite result was given by the addition of Mn3O4 molars. In the photocatalytic test, the best results were shown by the Ag/TiO2/Mn3O4 nanocomposite with the dominance of Mn3O4 for UV radiation and visible light. Under optimum conditions, Ag/TiO2/Mn3O4 nanocomposite was able to degrade methylene blue up to 91% with irradiation for 2 hours. The scavenger test identified pits as the species that contributed most to this photocatalytic process. Reusability and stability tests on Ag/TiO2/Mn3O4 nanocomposites showed positive results. |
 S-indrianita_lionadi.pdf :: Unduh
|
| No. Panggil : | S-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xiii, 49 pages: illustration |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-pdf | 14-22-80278935 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20499721 |