Pembuatan karbon aktif termodifikasi NiO dari cangkang kelapa sawit sebagai CO2 scrubber pada controlled atmosphere storage = Preparation of NiO-modified activated carbon from palm kernel shells as CO2 scrubber in controlled atmosphere storage
Muhammad Jihadilan Aliansyah Putra;
Yuliusman, supervisor; Sutrasno Kartohardjono, examiner; Eva Fathul Karamah, examiner
(Fakultas Teknik Universitas Indonesia, 2020)
|
|
Controlled Atmosphere Storage memiliki CO2 Scrubber yang dapat dikembangkan melalui pengembangan adsorben karbon aktif. Produksi karbon aktif dapat dibuat dengan bahan baku biomassa, salah satunya ialah cangkang kelapa sawit yang memiliki kandungan karbohidrat struktural lignin (53,85%), hemiselulosa (26,16%), dan selulosa (6,92%). Produksi karbon aktif berbahan baku cangkang kelapa sawit melalu mekanisme preparasi bahan baku. Langkah pertama adalah aktivasi kimia dengan merendamkan cangkang kelapa sawit dalam larutan KOH selama 24 jam dan dilanjutkan dengan karbonisasi pada suhu 350oC. Lalu aktivasi kimia kedua dengan variasi rasio KOH : karbon aktif 2:1 dan 4:1 sebelum diaktivasi scara fisika menggunakan gas N2 dengan laju alir 150 ml/menit selama 60 menit pada suhu 800 ᵒC. Hasil karbon aktif terbaik didapat pada rasio 2:1 dengan Bilangan Iod, Luas Permukaan, dan yield berturut-turut 1216,28 mg/g; 1209,78 m2/g; dan 39,01%. Modifikasi karbon aktif yang bertujuan meningkatkan kemampuan adsorpsi CO2 dilakukan dengan perendaman dalam larutan logam NiO dengan variasi loading 0,5%, 1%, dan 2%. Hasil adsorpsi gas CO2 dengan gas analyzer terbaik didapat pada variasi loading 2% dengan presentase adsorpsi sebesar 19,1%. Controlled Atmosphere Storage has a CO2 Scrubber that can be improved through the development of activated carbon adsorbents. The production of activated carbon can be made with biomass raw materials, one of which is a palm kernel shell which has structural carbohydrate content of lignin (53.85%), hemicellulose (26.16%), and cellulose (6.92%). Production of activated carbon made from palm kernel shells is through the mechanism of preparation of raw materials. The first step is chemical activation by immersing the palm kernel shell in a KOH solution for 24 hours and followed by carbonization at 350 °C. Then the second chemical activation with a variation of the ratio of KOH: activated carbon 2:1 and 4:1 before being physically activated using N2 gas with a flow rate of 150 ml /min for 60 minutes at a temperature of 800 °C. The best activated carbon yield was obtained at a ratio of 2:1 with Iodic Number, Surface Area, and yield respectively 1216.28 mg/g; 1209.78 m2/g; and 39.01%. Modification of activated carbon which aims to increase the ability of CO2 adsorption is done by immersion in a NiO metal solution with loading variations of 0.5%, 1%, and 2%. The best result of CO2 gas adsorption with gas analyzer were obtained at a loading variation of 2% with an adsorption percentage of 19.1%. |
 S-Muhammad Jihadilan Aliansyah Putra.pdf :: Unduh
|
| No. Panggil : | S-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2020 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xv, 82 pages: illustration; appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-pdf | 14-22-53763694 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20504669 |