Efek penambahan grafin dan waktu sonikasi terhadap performa baterai Li4Ti5O12-Sn nano sebagai material anoda baterai ion litium = Effect of graphene addition and sonication time to battery performance of Li4Ti5O12-Sn nano as anode material for Li-ion battery
Pierre Wolter Winowatan;
Anne Zulfia, supervisor; Bambang Priyono, supervisor; Rahmat Saptono, examiner; Achmad Subhan, examiner
(Fakultas Teknik Universitas Indonesia, 2020)
|
|
Pembuatan komposit Li4Ti5O12-Sn nano/Grafin telah berhasil dilakukan sebagai material anoda pada baterai ion litium. Penambahan material grafin komersial dengan variasi berat 1%, 3% dan 5% dan waktu sonikasi selama 45 menit dan 75 menit telah dilaksanakan. Sintesis dari Li4Ti5O12 dilakukan dengan membuat prekursor TiO2 menggunakan metode sol-gel dan sudah dikalsinasi yang dicampurkan dengan LiOH dengan metode solid-state reaction dan proses sintering. Material Li4Ti5O12 dicampurkan dengan serbuk Sn nano dengan berat 10% untuk mendapatkan material komposit Li4Ti5O12-Sn nano. Pembuatan komposit Li4Ti5O12-Sn nano/Grafin dimulai dari penambahan variasi berat grafin komersial yang berbeda dengan metode wet milling menggunakan planetary ball mill selama 1 jam dan dilanjutkan dengan proses sonikasi menggunakan ultrasonic homogenizer dengan variasi waktu berbeda sebelum akhirnya dilakukan kalsinasi menggunakan vacuum furnace dengan gas N2 pada temperatur 500°C selama 5 jam. Hasil penelitian menunjukan bahwa adanya peningkatan performa dilihat dari kapasitas spesifik dari komposit Li4Ti5O12-Sn nano dengan penambahan berat grafin yang optimum pada 5% dengan waktu sonikasi 75 menit walaupun terdapat beberapa pengotor yang terdeteksi pada hasil pengujian XRD. Secara umum performa baterai sangat baik pada siklus yang tinggi dengan pengurangan discharge capacity yang minor dan dengan penambahan grafin dapat meningkatkan kapasitas spesifik dari material komposit Li4Ti5O12-Sn nano. The synthesis of Li4Ti5O12-Sn nano/Graphene composite has been successfully carried out as an anode material for lithium-ion battery. The addition of commercial graphene with a weight variation of 1%, 3% and 5% and sonication time of 45 minutes and 75 minutes has been done successfully. Synthesis of Li4Ti5O12 is done by making TiO2 precursors using sol-gel method and has been calcined, followed by solid-state reaction with LiOH sintering process. The Li4Ti5O12 material is mixed with Sn nano powder with a weight of 10% to obtain L4Ti5O12-Sn nano composite material. Production of Li4Ti5O12-Sn nano/Graphene composites start from mixing different commercial graphene weight variations by wet milling method using planetary ball mill for 1 hour and continued with sonication process using ultrasonic homogenizer with different time variations before calcination process using a vacuum furnace with N2 gas at 500°C for 5 hours. Li4Ti5O12-Sn nano with an optimal maximum weight at 5% with a sonication time of 75 minutes including some impurities reported on the XRD results. In general, the battery samples are very good at high cycles with overall small capacity fade. |
 T-Pierre Wolter Winowatan.pdf :: Unduh
|
| No. Panggil : | T-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2020 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xi, 45 pages : illustration ; appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| T-pdf | 15-22-53297156 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20505095 |