Pengaruh proses leaching pada roasted slag feronikel dengan variasi 6 dan 8 m asam klorida sebagai agen pelindi terhadap recovery magnesium = Effect of leaching process on roasted slag ferronickel with variation 6 and 8 m hydrocloric acid as leaching agent against magnesium recovery.
Jordan Andrean Martin;
Reza Miftahul Ulum, supervisor; Wahyuaji Narottama Putra, examiner; Jaka Fajar Fatriansyah, examiner
(Fakultas Teknik Universitas Indonesia, 2020)
|
|
Paduan Feronikel (FeNi) merupakan salah satu produk utama yang dihasilkan dalam pengolahan bijih nikel laterit. Negara Indonesia merupakan salah satu negara dengan deposit nikel besar dalam bentuk bijih laterit. Penelitian ini bertujuan untuk meningkatkan kadar senyawa Magnesium melalui proses leaching menggunakan larutan asam klorida dengan variasi konsentrasi larutan dan waktu proses leaching. Sampel yang digunakan berupa Slag Feronikel yang telah diberikan penambahan aditif Na2CO3 dan telah dipanggang dengan temperatur 1100oC. Penelitian dilakukan dengan melakukan proses leaching sampel menggunakan larutan HCl 4M dan 6M. Proses leaching untuk setiap konsentrasi larutan kemudian divariasikan waktu proses leaching yang digunakan yaitu 2, 4, dan 6 Jam. Setelah proses leaching mencapai waktu yang ditentukan, dilakukan proses penyaringan untuk memisahkan filtrat dan residu yang dihasilkan. Pada filtrat hasil leaching dilakukan karakterisasi ICP-OES untuk mengidentifikasi unsur-unsur yang terlarut pada filtrat selama proses leaching berlangsung. Sedangkan residu hasil leaching dilakukan karakterisasi SEM/EDS untuk mengetahui perubahan yang terjadi pada residu setelah proses leaching. Hasil dari penelitian ini menunjukkan bahwa adanya peningkatan kadar Magnesium dari kadar sebelum dilakukan proses leaching. Proses leaching menggunakan larutan HCl 6M menghasilkan peningkatan kadar Magnesium yang lebih besar. Selain itu, waktu proses leaching yang digunakan juga berpengaruh terhadap hasil yang dilakukan, dimana proses leaching Roasted Slag Feronikel memiliki waktu optimal untuk proses ekstraksi senyawa Magnesium. Berdasarkan hasil penelitian ini, dapat disimpulkan bahwa larutan asam klorida (HCl) yang digunakan dalam proses leaching Roasted Slag Feronikel dapat meningkatkan kadar senyawa Magnesium pada filtrat. Proses leaching yang paling optimal pada penelitian ini menggunakan larutan HCl 6M selama 4 Jam, dengan persentase leaching sebesar 49,05%. Feronickel Alloy (FeNi) is one of the main products produced in the processing of nickel laterite ore. Indonesia is one of the countries with a large nickel deposit in the form of laterite ore. This research aims to increase the levels of Magnesium compounds through the leaching process using hydrochloric acid solutions with varying solution concentrations and leaching process times. The sample used is the Feronickel Slag which has been given the addition of the Na2CO3 additive and has been baked at an 1100oC temperature. Research is conducted by conducting leaching process samples using a solution of HCl 4M and 6M. The leaching process for each solution concentration is then varied when the leaching process used are 2, 4, and 6 hours. After the leaching process reaches the specified time, the filtering process is performed to separate the filtrate and the resulting residue. In filtrate, leaching is performed ICP-OES characterization to identify the dissolved elements of the filtrate during the progress of the leaching process. Meanwhile, leaching residue is performed SEM/EDS characterization to know the changes occurring in residue after leaching process. The results of this study showed that the presence of increased levels of Magnesium from levels prior to leaching processes. The leaching process using a 6M HCl solution produces a greater increase in Magnesium levels. In addition, the leaching process time used also affects the results, where the leaching process of Roasted Slag Feronickel has the optimal time for the extraction process of Magnesium compounds. Based on the results of this study, it can be concluded that a solution of hydrochloric acid (HCl) used in the leaching process of Roasted Slag Feronikel can increase the levels of Magnesium compounds in filtrate. The most optimal leaching process in this study was using an 6M HCl solution for 4 hours, with a leaching percentage of 49,05%. |
 Pdf-Jordan Andrean Martin.pdf :: Unduh
|
| No. Panggil : | S-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2020 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda. |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xii, 53 pages : illustration. |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-pdf | 14-21-619699341 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20505271 |