Degradasi Mikroplastik melalui Proses Oksidasi Lanjut Menggunakan Kombinasi Proses Ozonasi dan Hidrogen Peroksida = Degradation of Microplastic by Advanced Oxidation Process Using a Combination of Ozonation and Hydrogen Peroxide.

Devita Amelia; Eva Fathul Karamah, supervisor; Setijo Bismo, examiner; Nelson Saksono, examiner; Tania Surya Utami, examiner (Fakultas Teknik Universitas Indonesia, 2020)

 Abstrak

ABSTRAK
Pada penelitian ini dilakukan upaya degradasi mikroplastik polietilena dengan proses
oksidasi lanjut menggunakan metode ozonasi dan metode kombinasi ozonasi dengan
hidrogen peroksida. Kinerja dan keefektifan kedua konfigurasi metode dalam
mendegradasi mikroplastik dianalisis berdasarkan persentase penurunan berat (metode gravimetrik) yang diintegrasikan dengan analisis perubahan struktur kimia (FT-IR) dan perubahan morfologi permukaan mikroplastik (SEM) dengan memvariasikan pH awal larutan dan laju alir gas ozon. Metode kombinasi ozonasi dengan hidrogen peroksida pada pH 12 dan laju alir gas ozon 3 L/menit menunjukkan hasil yang efektif dalam mendegradasi mikroplastik polietilena ditandai dengan persentase penurunan berat mikroplastik yang paling besar. Analisis FT-IR menunjukkan bahwa terjadinya pembentukan gugus fungsi hidroksil, peroksil dan karbonil. Analisis SEM menunjukkan bahwa permukaan mikroplastik terbentuk rongga dan kerutan yang mempresentasikan terjadinya degradasi pada mikroplastik. Mekanisme degradasi mikroplastik telah diusulkan. Data saat ini menunjukkan bahwa metode kombinasi ozonasi dengan hidrogen peroksida dapat menjadi pendekatan yang potensial untuk mendegradasi limbah mikroplastik.

ABSTRACT
In this study an attempt was made to polyethylene microplastic degradation by advanced oxidation process using ozonation methods and a combination of ozonation methods with hydrogen peroxide. The performance and effectiveness of the two method configurations for microplastic degradation were analyzed based on percentage weight loss (gravimetric method) integrated with analysis of chemical structure change (FT-IR) and changes in microplastic surface morphology (SEM) by varying the initial pH of the solution and the ozone gas flow rate. The combination method of ozonation with hydrogen peroxide at pH 12 and ozone gas flow rate of 3 L/min shows effective results in degrading the polyethylene microplastics characterized by the greatest percentage of microplastic
weight loss. FT-IR analysis shows that the hydroxyl, peroxyl and carbonyl functional
groups are formed. SEM analysis shows that the surface of the microplastic is formed
cavities and wrinkles which represent the degradation of the microplastic. Mechanism of
microplastic degradation has been proposed. The present data suggest that a combination
method of ozonation and hydrogen peroxide could be a potential appoarch for degradation
of microplastic waste.

 File Digital: 1

Shelf
 T-Devita Amelia.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : T-Pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Subjek :
Penerbitan : Depok: Fakultas Teknik Universitas Indonesia, 2020
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xv, 80 pages : illustration ; appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
T-Pdf 15-22-75297098 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20505982