Sintesis nanopartikel LiFePO4 dengan pendekatan green synthesis menggunakan ekstrak daun delima (punica granatum l.) dan uji kinerja elektrokimianya sebagai bahan katoda dalam baterai ion litium = Synthesis of LiFePO4 nanoparticles with green synthesis approach using pomegranate (punica granatum l.) leaf extract and the electrochemical performance test as cathode material in lithium ion battery.

Zena Stitya Rosenta; Yoki Yulizar, supervisor; Achmad Subhan, supervisor; Ivandini Tribidasari Anggraningrum, examiner; Sumardi, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020)

 Abstrak

Pada penelitian ini, nanopartikel Li3PO4, Fe3(PO4)2, LiFePO4 sampel A telah berhasil disintesis menggunakan ekstrak daun delima (Punica granatum L) dengan metode green synthesis dan nanopartikel LiFePO4 sampel B telah berhasil disintesis dengan metode kimia (sol-gel). Ekstrak daun delima (EDD) yang dihasilkan mengandung senyawa metabolit sekunder yang berfungsi sebagai sumber basa dan capping agent dalam menstabilkan ukuran nanopartikel dan mencegah terjadinya proses aglomerasi. Hasil karakterisasi FTIR menunjukkan bahwa LiFePO4 sampel A dan B membentuk serapan vibrasi (v2-v4) PO43- pada bilangan gelombang 586 cm-1 - 461 cm-1 (v4 & v2) dan 1038/1035 cm-1 (v3). Pada hasil XRD menunjukkan nanopartikel LiFePO4 sampel A dan B memiliki sistem kristal orthorombik. Hasil SEM menunjukkan morfologi LiFePO4 memiliki bentuk yang heterogen. Nanopartikel LiFePO4 yang telah disintesis kemudian dijadikan sebagai lembaran katoda dan disusun menjadi baterai ion litium kemudian dilakukan karakterisasi elektrokimia menggunakan EIS, CV dan GCD. Hasil uji GCD menunjukkan bahwa sampel A memiliki kapasitas discharge sebesar 0,35 mAH/gram sedangkan sampel B memiliki kapasitas discharge sebesar 0,93 mAH/gram.

In this research, Li3PO4, Fe3(PO4)2, LiFePO4 nanoparticles sample A have been successfully synthesized using pomegranate leaf extract (Punica granatum L) with green synthesis method and LiFePO4 nanoparticle sample B have also been successfully synthesized by chemical method (sol-gel). Pomegranate leaf extract (EDD) produced contains secondary metabolite compounds that function as a source of base and capping agent in stabilizing the size of nanoparticles and preventing agglomeration. The results of FTIR characterization shows that the LiFePO4 nanoparticles of samples A and B forms vibrational absorption (v2-v4) PO43- at wavenumbers 586-461 cm-1 (v4 & v2) and 1038/1035 cm-1 (v3). The XRD results show that the LiFePO4 nanoparticles of samples A and B have an orthorhombic crystal system. SEM results show that the morphology of LiFePO4 has a heterogeneous shape. The LiFePO4 nanoparticles that were formed were successfully used as cathode sheets and arranged into lithium ion batteries then electrochemical characterization was carried out using EIS, CV and GCD. The GCD test results show that sample A has a discharge capacity of 0,35 mAH/gram while sample B has a discharge capacity of 0,93 mAH/gram.

 File Digital: 1

Shelf
 S-Pdf-Zena Stitya Rosenta.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : S-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xvii, 86 pages : illustration ; appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S-pdf 14-21-315375389 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20508381