Preparasi komposit busa nikel termodifikasi graphene dan MnO2 sebagai superkapasitor = Preparation of graphene and MNO2 modified nickel foam composites as supercapacitors
Salsabila Dinitasari;
Ivandini Tribidasari Anggraningrum, supervisor; Rahmat Wibowo, supervisor; Yoki Yulizar, examiner; Dita Arifa Nurani, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020)
|
|
Pada penelitian ini preparasi komposit busa nikel termodifikasi mangan oksida dan graphene dan uji performanya sebagai elektroda untuk superkapasitor telah berhasil dilakukan. Karakterisasi menggunakan SEM-EDX menunjukkan morfologi berupa bercak putih dan terbentuknya lapisan berupa lembaran yang menyelimuti kerangka busa nikel menunjukkan keberadaan mangan oksida dan graphene. Sedangkan karakterisasi dengan Spektroskopi Raman menunjukkan adanyaÃÂàpeakÃÂàyang mengindikasikanÃÂàD bandÃÂàdanÃÂàG bandÃÂàÃÂàdengan rasio ID/IGÃÂàyang dapat menentukan keberadaan material elektroaktif graphene.ÃÂàUji elektrokimia menggunakan teknikÃÂàCyclic VoltammetryÃÂà(CV) menunjukkan nilai kapasitansi spesifik tertinggi pada Busa nikel/MnO2/GrapheneÃÂàyaitu sebesar 1117,32 F/g padaÃÂàscanrateÃÂàoptimum 5 mV.s-1. Uji elektrokimia menggunakan teknikÃÂàGalvanostatic Charge-dischargeÃÂà(GCD) menunjukkan performa terbaik adalah padaÃÂàBusa nikel/MnO2/Graphene pada arus yang diberikan sebesar 2 mA, dengan nilai kapasitansi spesifik mencapai 977,77 F/g, densitas energi sebesar 27,5 Wh/kg dan densitas daya sebesar 4500 W/kg. Uji elektrokimia menggunakan teknikÃÂàElectrochemical Impedance SpectroscopyÃÂà(EIS) menghasilkan Nyquist plot.ÃÂàNilaiÃÂàRctÃÂàÃÂàdiperoleh untuk masing-masing elektrodaÃÂàbusa nikel/MnO2, busa nikel/graphene, dan busa nikel/MnO2/graphene adalah sebesar 415ÃÂàÃÂé; 580,58 ÃÂé; dan 1460 ÃÂé. In this research, the preparation of nickel foam composites modified with manganese oxide and graphene and its performance test as electrodes for supercapacitor has been successfully carried out. Characterization using SEM-EDX showed morphology in the form of white spots and the formation of a layer in the form of a sheet covering the nickel foam framework indicating the presence of manganese oxide and graphene. Meanwhile, the characterization using Raman spectroscopy showed that there was a peak indicating the D band and G band with the ID/IGÃÂàratio which could determine the presence of graphene electroactive material. The electrochemical test using the Cyclic Voltammetry (CV) technique showed the highest specific capacitance value for MnO2/graphene/Ni foam, which was 1117.32 F/g at an optimum scan rate of 5 mV.s-1. The electrochemical test using the Galvanostatic Charge-discharge (GCD) technique shows that the best performance is on MnO2/graphene/Ni foam at a given current of 2 mA, with a specific capacitance value of 977.77 F/g, an energy density of 27.5 Wh/kg and a power density of 4500 W/kg. Electrochemical tests using the Electrochemical Impedance Spectroscopy (EIS) technique produced a Nyquist plot. The Rct value obtained for each electrode of MnO2/Ni foam , graphene/Ni foam, and MnO2/graphene/Ni foam is 415 ÃÂé; 580.58 ÃÂé; and 1460 ÃÂé. |
 S-Pdf-Salsabila Dinitasari.pdf :: Unduh
|
| No. Panggil : | S-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xviii, 53 pages : illustration ; appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-pdf | 14-22-90732597 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20508521 |