Preparasi nikel mangan oksida pada busa nikel sebagai Katalis Anoda pada Direct Urea Fuel Cell = Preparation of nickel manganese oxide modified ni foam for Anode Catalyst Direct Urea Fuel Cell
Yola Yolanda;
Ivandini Tribidasari Anggraningrum, supervisor; Muhammad Ridwan, supervisor; Rahmat Wibowo, examiner; Iman Abdullah, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020)
|
|
Fuel cell urea membutuhkan katalis berbasis logam Ni. Tetapi logam Ni memiliki sifat over potensial yang tinggi sehingga menurunkan efisensi fuel cell. Doping dengan MnO2 dapat menurunkan over potensial Ni. Oleh karena itu pada penelitian ini NiMn2O4 dideposisi dengan metode hidrotermal pada permukaan busa nikel untuk digunakan sebagai katalis pada anoda fuel cell urea. Pendeposisian dilakukan pada struktur busa nikel yang berpori menggunakan larutan Mn(NO3)2.6H2O dan Ni(NO3)2.6H2O sebagai prekusor nikel dan mangan dengan kehadiran urea. Reaksi dilakukan autoclave dan dipanaskan di dalam furnace dengan suhu 180° C selama 24 jam. Dilanjtkan dengan annealing pada 400° C selama 2 jam. Hasil penelitian menunjukkan bahwa busa nikel telah berhasil dimodifikasi dengan NiMn2O4. NiMn2O4/busa nikel menunjukkan densitas arus yang baik untuk fuel cell urea berdasarkan hasil cyclic voltammetry. Variasi konsentrasi prekusor nikel dan mangan pada rasio 1:1 menunjukkan hasil terbaik dengan densitas arus sebesar 206.453 mA cm-2 didalam larutan 2 M KOH dan 0.33 M Urea. Aplikasi pada Direct Urea Fuel Cell menunjukkan densitas daya yang dihasilkan adalah 0.304 mW cm-2 dengan mengunakan larutan 2 M KOH dan 0.33 M Urea dalam anoda dan larutan 2 M H2O2 dan 2 M H2SO4 pada katoda. ABSTRACT Urea fuel cells require a Ni metal-based catalyst. However, Ni metal has high over potential properties, thus reducing fuel cell efficiency. Doping with MnO2 can reduce the over potential of Ni. Therefore, in this study NiMn2O4 was deposited by hydrothermal method on the surface of nickel foam to be used as a catalyst in the urea fuel cell anode. The deposition was carried out on the porous nickel foam structure using a solution of Mn(NO3)2.6H2O and Ni(NO3)2.6H2O as a precursor to nickel and manganese in the presence of urea. The reaction is autoclaved and heated in a furnace at 180 ° C for 24 hours. Continued with annealing at 400 ° C for 2 hours. The results showed that nickel foam was successfully modified with NiMn2O4. NiMn2O4 / nickel foam shows good current density for urea fuel cells based on cyclic voltammetry results. The variation in the concentration of nickel and manganese precursors at a 1: 1 ratio showed the best results with a current density of 206,453 mA cm-2 in a 2 M KOH solution and 0.33 M Urea. Application to the Direct Urea Fuel Cell shows that the resulting power density is 0.304 mW cm-2 using a 2 M KOH solution and 0.33 M Urea in the anode and a 2 M H2O2 and 2 M H2SO4 solution at the cathode. |
 S-pdf-Yola Yolanda.pdf :: Unduh
|
| No. Panggil : | S-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xiii, 39 pages : illustrations ; |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-pdf | 14-21-527988435 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20508546 |