Sintesis dan karakterisasi nanokomposit selulosa/Ag3PO4/ZnO untuk fotokatalisis degradasi metil jingga = Synthesis and characterization of cellulose/Ag3PO4/ZnO nanocomposite for photocatalytic degradation of methyl orange

Sitanggang, Ida Frisca Royani; Helmiyati, supervisor; Yoki Yulizar, examiner; Dita Arifa Nurani, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020)

 Abstrak

Nanokomposit selulosa/Ag3PO4/ZnO untuk fotokatalisis degradasi metil jingga telah disintesis dan dikarakterisasi menggunakan FTIR, XRD, UV-DRS dan SEM. Penambahan Ag3PO4 pada ZnO dapat menurunkan energi band gap ZnO dari 3.21 eV menjadi 3.19 eV. Pada penelitian ini, ZnO akan bertindak sebagai sisi aktif katalis, Ag3PO4 bertindak sebagai sensitizer yang dapat meningkatkan kemampuan katalis untuk menyerap sinar visible, sedangkan selulosa bertindak sebagai support katalis. Proses fotokatalisis degradasi metil jingga dilakukan di bawah sinar UV dan visible selama 1 jam. Kondisi optimum yang diperolah adalah ketika proses fotokatalisis dilakukan pada pH 6, menggunakan jumah katalis 45 mg, dengan rasio komposit pada ZnO/Ag3PO4 1:2, dan rasio selulosa pada nanokomposit selulosa/Ag3PO4/ZnO 1:2:1.  Nilai efisiensi fotodegradasi metil jingga yang paling tinggi adalah sebesar 81.05%. Reaksi ini mengikuti kinetika pseudo orde satu dan proses adsorpsi yang terjadi mengikuti model isoterm adsorpsi Langmuir.

Cellulose/Ag3PO4/ZnO nanocomposite for photocatalytic degradation of methyl orange have been synthesized and characterized by FTIR, XRD, UV-DRS, and SEM. The addition of Ag3PO4 to ZnO can reduce the band gap energy from 3.21 eV to 3.19 eV. In this work, ZnO acts as an active site, Ag3PO4 acts as sensitizer that can increase the ability of catalyst to absorb visible light, and cellulose acts as a catalyst support. The photocatalysis degradation of methyl orange was observe under UV and light illumination for an hour. The optimum condition obtained was when the photocatalyst was conducted at pH 6 using 45 mg catalyst with composite ratio ZnO/Ag3PO4 1:2, and cellulose ratio on cellulose/Ag3PO4/ZnO nano composite 1:2:1. The highest photodegradation efficiency of methyl orange is 81.05%. This reaction fits well to the pseudo-first order kinetics and Langmuir adsorption isotherm model.

 File Digital: 1

Shelf
 Pdf-Sitanggang, Ida Frisca Royani.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : S-pdf
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : computer
Tipe Carrier : online resource
Deskripsi Fisik : xiii, 52 pages : illustration ; appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S-pdf 14-21-873386999 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20508733