Nanokomposit alginat-CMC/Fe3O4/CaO sebagai katalis untuk sintesis Fatty Acid Methyl Ester (FAME) dari waste cooking oil = Alginate-CMC/Fe3O4/CaO nanocomposite as a catalyst for synthesis of Fatty Acid Methyl Ester (FAME) from waste cooking oil
Irhami Werda Sudana;
Helmiyati, supervisor; Rika Tri Yunarti, supervisor; Yoki Yulizar, examiner; Sunardi, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020)
|
|
Pada penelitian ini, nanokomposit Alginat-CMC/Fe3O4/CaO telah berhasil disintesis dan didukung dengan karakterisasi FTIR diperoleh bilangan gelombang 573 cm-1 dan 423 cm-1 menunjukkan vibrasi ulur Fe-O dan Ca-O, dengan XRD diperoleh puncak gabungan dari biopolimer Alginat-CMC dan Fe3O4/CaO, dan SEM-Mapping diperoleh Fe3O4/CaO berbentuk bulat yang tersebar secara merata pada permukaan alginat-CMC dan TEM diperoleh diameter berkisar 16.193 nm. Biopolimer alginat-CMC berperan sebagai pendukung dari katalis Fe3O4/CaO. Nanokomposit digunakan sebagai katalis untuk produksi biodiesel dari WCO melalui reaksi transesterifikasi diperoleh kondisi terbaik dengan rasio massa CaO terhadap Fe3O4 (1:2), rasio massa antara Fe3O4/CaO terhadap Alginat-CMC (2:2), jumlah katalis terbaik 0.9%wt dan reaksi selama 120 menit dari WCO menjadi biodiesel dengan yield sebesar 89.27%. Sifat fisik dari metil ester sesuai dengan SNI dan ASTM D6751 dengan massa jenis (40°C) 0.890 g/ml, FFA 0,254 % dan bilangan asam 0,542 mgKOH/g. Hasil karakterisasi biodiesel dengan GC-MS diperoleh metil ester dengan kelimpahan relatif terbesar adalah 9-octadecenoic acid (Z)-methyl ester. Studi kinetika reaksi mengikuti pseudo - orde pertama dengan hukum laju reaksi v = k[WCO] dengan nilai konstanta laju reaksi 0.0152 menit-1. In this study, Alginate-CMC/Fe3O4/CaO nanocomposite were successfully synthesized and supported by FTIR characterization, obtained wave numbers of 573 cm-1 and 423 cm-1 showing strain vibrations of Fe-O and Ca-O, with peak XRD obtained the combination of Alginate-CMC and Fe3O4/CaO, and SEM-Mapping obtained a rounded Fe3O4/CaO composite that was evenly distributed on the surface of the alginat-CMC and TEM obtained an diameter size of about 16.193 nm. The Alginate-CMC as a support material for the Fe3O4/CaO catalyst. Nanocomposite are used as catalysts for biodiesel production from waste cooking oil through transesterification reactions, the best conditions are obtained with the mass ratio of CaO to Fe3O4 (1:2), Fe3O4/CaO to Alginate-CMC (2:2), the amount of catalyst is 0.9wt% and reaction for 120 minutes with yield is 89.27%. Physical properties of methyl ester according to the SNI and ASTM D6751 obtained a density (40°C) of 0.890 g/ml, FFA 0.254% and an acid number of 0.542 mgKOH/g. The results of biodiesel characterization by GC-MS obtained the methyl ester with the largest relative abundance is 9-octadecenoic acid (Z)- methyl ester. The study of reaction kinetics followed the first pseudo-order with the law of reaction rate v = k[WCO] with a constant value of reaction rate 0.0152 minutes-1. |
 S-Irhami Werda Sudana .pdf :: Unduh
|
| No. Panggil : | S-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xix, 85 pages : illustration ; appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-pdf | 14-22-18694534 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20514253 |