Sintesis nano komposit hidroksiapatit/β-Trikalsium fosfat/alginat tersubtitusi magnesium secara ex-situ = Synthesis of hydroxyapatite/β-Tricalcium phosphate/alginate substituted magnesium nanocomposites ex-situ
Muhammad Rafi Tauchid Nugroho;
Nurlely, supervisor; Ariadne Lakshmidevi Juwono, examiner; Djonaedi Saleh, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2021)
|
|
Hidroksiapatit adalah material yang banyak digunakan untuk aplikasi implan tulang, karena mempunyai komposisi kimia yang sama dengan tulang manusia. Biphasic Calcium Phosphate (BCP) adalah campuran dari non-resorbable Hidroksiapatit (HA) dan resorbable β-Tricalcium Phosphate (β-TCP). Doping ion magnesium ke dalam HA/β-TCP akan membawa perbaikan pada reaksi biologis. Pada penelitian ini sintesis Mg-HA diiradisi dengan gelombang mikro menggunakan daya 720 watt selama 10 menit, dengan variasi substitusi Mg(OH)2 0.1M, 0.2M, dan 0.3M. Serbuk Mg-HA yang terbentuk disinter pada suhu 1300˚ C selama 3 jam untuk membentuk fasa biphasik Mg-HA/β-tricalcium phosphate kemudia dikarakterisasi dengan XRD. Sintesis nano-komposit Mg-HA/Alginat dilakukan dengan mencampurkan serbuk hasil sintering dengan alginat dan CaCl2 sebagai agen taut silang (cross linker agent). Larutan campuran diaduk menggunakan magnetic stirrer selama 3 jam kemudian dibiarkan selama 24 jam agar pencampuran sempurna. Metode karakterisasi komposit Mg-HA/β-TCP/Alginat menggunakan FTIR dan SEM-EDX. Hasil XRD menunjukan subtitusi Mg mereduksi ukuran kristal, parameter kisi dan indeks kristalinitas. Perlakuan thermal hingga suhu 1300 ˚ C pada HA membentuk dua fasa yaitu HA dan β-TCP. SEM-EDX menunjukan bahwa partikel yang terdapat pada komposit Mg-HA/β-TCP/Alginat berukuran tidak sama mempengaruhi grain growth. Hydroxyapatite is a material that is widely used for bone implant applications because it has the same chemical composition as human bone. Biphasic Tricalcium Phosphate (BCP) is a mixture of non-resorbable hydroxyapatite (HA) and resorbable β-Tricalcium Phosphate (β-TCP). Doping of magnesium ion into HA/β-TCP will bring about improvement in biological reactions. In this study, the synthesis of Mg-HA was irradiated with microwaves using 720 watts of power for 10 minutes, with variations of 0.1M, 0.2M, and 0.3M Mg (OH)2 substitution. The Mg-HA powder formed was sintered at 1300˚C for 3 hours to form a biphasic phase of Mg-HA/β-tricalcium phosphate which was then characterized by XRD. The synthesis of Mg-HA/Alginate nano-composites was carried out by mixing the sintered powder with alginate and CaCl2 as a cross-linker agent. The mixed solution was stirred using a magnetic stirrer for 3 hours then left for 24 hours for complete mixing. The characterization method for Mg-HA / β-TCP / Alginate composites used FTIR and SEM-EDX. XRD results showed that Mg substitution reduced crystal size, lattice parameters, and crystallinity index. Thermal treatment up to a temperature of 1300 ˚ C on HA forms two phases, namely HA and β-TCP. SEM-EDX showed that the particles contained in the Mg-HA/β-TCP/Alginate composite had different sizes affecting grain growth. |
 S-Muhammad Rafi Tauchid Nugroho.pdf :: Unduh
|
| No. Panggil : | S-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2021 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xi, 45 pages : illustration + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-pdf | 14-22-45718790 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20515022 |