Sifat Mekanik Komposit Epoksi/Serat Daun Nanas Subang Anyam dengan Variasi Orientasi Arah Serat yang Dipabrikasi dengan Metode Hand Lay-Up Diikuti Dengan Vacuum Bagging = Mechanical Properties of Woven Subang Pineapple Leaf Fiber/Epoxy with Fiber Orientation Variations, Fabricated by Hand Lay-Up Followed by Vacuum Bagging Methods
Randito Ananta Pratama;
Ariadne Lakshmidevi Juwono, supervisor; Seto Roseno, supervisor; Djonaedi Saleh, examiner; Budhy Kurniawan, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020)
|
Serat daun nanas bisa menjadi pengganti penggunaan serat sintetis dikarenakan sifatnya yang ramah lingkungan dan tersedia di Indonesia. Tujuan penelitian ini untuk memperoleh sifat mekanik papan komposit epoksi/serat daun nanas Subang dianyam. Komposit difabrikasi dengan variasi orientasi arah serat. Fabrikasi diawali dengan perlakuan alkali pada serat daun nanas Subang dan penganyaman. Fabrikasi komposit dengan metode hand lay-up kemudian diikuti dengan vacuum bagging. Hasil perhitungan densitas menunjukkan bahwa komposit epoksi/serat daun nanas Subang dengan orientasi arah 0°/0°/0°/0° dan 0°/90°/0°/90° termasuk dalam golongan papan serat kerapatan tinggi. Sifat Mekanik terbaik dimiliki oleh komposit epoksi/serat daun nanas Subang dengan orientasi arah serat 0°/0°/0°/0° yang memiliki kuat tarik sebesar (93,82 ± 22,48) MPa dan kuat lengkung sebesar (109,57 ± 8,11) MPa. Pengamatan dengan mikroskop optik menunjukkan bahwa serat daun nanas Subang dan epoksi menyatu dengan baik pada komposit epoksi/serat daun nanas Subang. Pineapple leaf fiber can be a substitute for synthetic fiber’s usage due to its eco-friendly nature and its availability in Indonesia. The purpose of this research was to obtain mechanical properties of Subang pineapple leaf fiber/epoxy composite board. The composite was fabricated with two fiber orientations. Fabrication was started by alkalization treatment towards the Subang’s pineapple leaf’s fiber. Composite fabrication was conducted by hand lay-up, followed by vacuum bagging method. The density measurement results showed that the composite Subang Pineapple Leaf Fiber / Epoxy with fiber orientation of 0°/0°/0°/0° and 0°/90°/0°/90° were categorized as high density boards. The best mechanical properties owned by Subang pineapple leaf fiber/epoxy composite with 0°/0°/0°/0° fiber orientation thad had tensile strength of (93,82 ± 22,48) MPa and flexural strength of (109,57 ± 8,11) MPa. The observation using optical microscope showed that the Subang pineapple leaf fiber and Epoxy had a strong interface. |
S-Randito Ananta Pratama.pdf :: Unduh
|
No. Panggil : | S-pdf |
Entri utama-Nama orang : | |
Entri tambahan-Nama orang : | |
Entri tambahan-Nama badan : | |
Subjek : | |
Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020 |
Program Studi : |
Bahasa : | ind |
Sumber Pengatalogan : | LibUI ind rda |
Tipe Konten : | text |
Tipe Media : | computer |
Tipe Carrier : | online resource |
Deskripsi Fisik : | xiv, 49 pages : illustration |
Naskah Ringkas : | |
Lembaga Pemilik : | Universitas Indonesia |
Lokasi : | Perpustakaan UI |
No. Panggil | No. Barkod | Ketersediaan |
---|---|---|
S-pdf | 14-22-22437773 | TERSEDIA |
Ulasan: |
Tidak ada ulasan pada koleksi ini: 20515218 |