Ketahanan korosi baja karbon AISI 4140 pada lingkungan panas bumi salinitas tinggi = Corrosion resistance of AISI 4140 carbon steel in high salinity geothermal environment
Riene Kaelamanda Pragitta;
Anawati, supervisor; Vivi Fauzia, examiner; Bambang Soegijono, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2022)
|
|
Korosi seragam dan pitting internal pada pipa sumur panas bumi umum terjadi karena fluida mengandung medium korosif garam dan CO2. Ketika terdapat gas CO2 yang terlarut dalam air, maka akan menyebabkan terjadinya korosi sweet. Garam cenderung terdisosiasi menjadi ion yang menyebabkan peningkatan konduktivitas listrik. Semakin tinggi konduktivitas, maka semakin tinggi kemampuan air garam untuk membawa arus listrik pada permukaan logam antara daerah anodik dan katodik, sehingga menghasilkan laju korosi yang lebih tinggi. Baja karbon AISI 4140 banyak digunakan sebagai material untuk pipa sumur panas bumi. Dalam penelitian ini, akan dilakukan analisis korosi baja karbon AISI 4140 di lingkungan dengan kadar garam tinggi yaitu 40950 mg/L NaCl + 5960 mg/L KCl + 2664 mg/L CaCl2. Pada tiap pengujian dilakukan dua variasi, yaitu dengan injeksi CO2 dan tanpa injeksi CO2. Berdasarkan hasil analis karakterisasi XRD, terdapat fasa Fe pada semua sampel dengan jenis larutan dengan dan tanpa injeksi CO2, namun pada sampel dengan larutan injeksi CO2 memiliki intensitas yang lebih kecil. Rendahnya intensitas fasa Fe mengindikasikan adanya deposit di permukaan sampel. Hasil analisis uji korosi menggunakan metode hilang berat menunjukan sampel yang dilakukan peredaman dalam larutan dengan injeksi CO2 menghasilkan penurunan massa yang lebih besar dibanding sampel yang diredam dalam larutan tanpa injeksi CO2. Hal ini didukung dengan laju korosi baja AISI 4140 pada larutan dengan injeksi CO2 lebih tinggi dibandingkan tanpa injeksi CO2 pada uji cyclic voltammetry. Tingginya laju korosi baja di lingkungan CO2 adalah akibat tingginya CO2 terlarut dalam air yang membentuk senyawa H2CO3 yang dapat menurunkan pH sehingga menjadikan larutan semakin korosif. Uniform corrosion and internal pitting of geothermal well pipes are common because the fluid contains the corrosive medium of salt and CO2. When there is CO2 dissolved in water, it will cause sweet corrosion. Salts tend to dissociate into ions causing an increase in electrical conductivity. The higher the conductivity, the higher the ability of the salt water to carry an electric current on the metal surface between the anodic and cathodic regions, resulting in a higher corrosion rate. AISI 4140 carbon steel is widely used as a material for geothermal well pipes. In this research, the corrosion analysis of AISI 4140 carbon steel will be carried out in an environment with high salt content, namely 40950 mg/L NaCl + 5960 mg/L KCl + 2664 mg/L CaCl2. In each test, two variations were performed, namely with CO2 injection and without CO2 injection. Based on the results of the XRD characterization analysis, there was a Fe phase in all samples with the type of solution with and without CO2 injection, but the sample with CO2 injection solution had a smaller intensity. The low intensity of the Fe phase indicates the presence of deposits on the sample surface. The results of the analysis of the corrosion test using the weight loss method showed that samples soaked in solution with CO2 injection resulted in a greater reduction in mass than samples soaked in solution without CO2 injection. This is supported by the corrosion rate of AISI 4140 steel in a solution with CO2 injection which is higher than without CO2 injection in the cyclic voltammetry test. The high rate of corrosion of steel in the CO2 environment is due to the high dissolved CO2 in water which forms H2CO3 compounds which can lower the pH, making the solution more corrosive. |
 S-Riene Kaelamanda Pragitta.pdf :: Unduh
|
| No. Panggil : | S-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2022 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource (rdcarrier) |
| Deskripsi Fisik : | xiii, 34 pages : illustration |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-pdf | 14-22-45263492 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20522560 |