Pengaruh Temperatur Sintering Terhadap Densitas, Kekerasan, dan Konduktivitas Termal pada Material Komposit Cu/Al/Cu dengan Metode Powder in Sealed Tube Rolling = Effect of Sintering Temperature on Density, Hardness and Thermal Conductivity of Cu/Al/Cu Composite Materials Using Powder in Sealed Tube Rolling Method
Dhika Tri Handoko;
Rahmat Saptono, supervisor; G., Shatrakov Y.; Jaka Fajar Fatriansyah, examiner
(Fakultas Teknik Universitas Indonesia, 2022)
|
|
Saat ini kebutuhkan akan computer/laptop semakin meningkat. Laptop dengan performa tinggi akan menghasilkan energi yang besar sehingga akan membuat laptop panas. Untuk menghindari hal tersebut maka dibutuhkan sistem pendingin. Saat ini system pendingin pada laptop terbuat dari tembaga. Tembaga memiliki kekurangan dimana biaya yang mahal serta berat. Karena hal tersebut maka ditambahkan aluminium untuk memangkas biaya serta membuat sistem pendingin yang lebih ringan tanpa mengurangi secara signifikan konduktivitas termal yang dimiliki tembaga. Pada penilitian ini akan menjelaskan mengenai metode powder in sealed tube dengan variable berupa temperatur sintering yaitu 3000C, 4000C, dan 5000C. Sampe yang sudah difabrikasi akan dilakukan karakterisasi dengan menggunakan SEM dan EDS untuk melihat strukturmikro yang dihasilkan. Selain itu juga dilakukan pengujian densitas, porositas, kekerasan, dan konduktivitas termal. Dari hasil yang didapat menyatakan bahwa semakin tinggi temperature sintering yang dilakukan maka akan semakin tinggi pula densitas yang dimiliki sampel serta akan menurunkan porositas. Selain itu seiring bertambahnya temperatur sintering nilai kekerasan dan konduktivitas termal pada sampel akan semakin meningkat. Currently the need for computers/laptops is increasing. Laptops with high performance will produce a lot of energy so that it will make the laptop hot. To avoid this, a cooling system is needed. Currently the cooling system on laptops is made of copper. Copper has the disadvantage of being expensive and heavy. Because of this, aluminum was added to cut costs and create a lighter cooling system without significantly reducing the thermal conductivity of copper. This research will explain about the powder in sealed tube method with variable sintering temperature, namely 3000C, 4000C, and 5000C. The fabricated samples will be characterized using SEM and EDS to see the resulting microstructure. In addition, density, porosity, hardness, and thermal conductivity tests were also carried out. From the results obtained, it is stated that the higher the sintering temperature, the higher the density of the sample and the lower the porosity. In addition, as the sintering temperature increases, the hardness and thermal conductivity of the sample will increase. |
 S-Dhika Tri Handoko.pdf :: Unduh
|
| No. Panggil : | S-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2022 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xiii, 54 pages : illustration + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-pdf | 14-23-94295007 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20525726 |