pengaruh substitusi cobalt pada sifat kemagnetan dan kelistrikan material Nd0,7Sr0,3Mn(1-x)CoxO3 (x = 0; 0,03; 0,05; 0,07 dan 0,1) = The effect of cobalt substitution on magnetic and electrical properties of Nd0,7Sr0,3Mn(1-x)CoxO3 (x = 0; 0,03; 0,05; 0,07 dan 0,1) material
Amilita Medisa Rizky Dharmayanti;
Djati Handoko, supervisor; Dwi Nanto, supervisor; Budhy Kurniawan, examiner; Dede Djuhana, examiner; Bambang Soegijono, examiner
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2021)
|
|
Penelitian mengenai polikristalin perovskite manganite telah dilakukan, material Nd0,7Sr0,3Mn(1-x)CoxO3 (x = 0; 0,03; 0,05; 0,07 dan 0,1) disintesis dengan menggunakan metode sol–gel kemudian dikarakterisasi dengan menggunakan Xray Diffractometer dan menunjukkan bahwa doping cobalt pada sampel tidak menyebabkan perubahan struktur kristal yaitu orthorhombic dengan space group Pnma. Karakterisasi Scanning Electron Microscopy menunjukkan bahwa terjadi perubahan ukuran grain yang membesar pada saat didoping cobalt sebesar 3% dan 7% akibat penurunan interaksi double exchange (DE). Hasil pengujian dengan menggunakan Vibrating Sampe Magnetometer menunjukkan penurunan magnetisasi pada saat diberikan kenaikan doping cobalt. Selain itu, saat diuji dengan cryogenic magnetometer, sampel dengan doping cobalt 7% menunjukkan nilai resistivitas yang tinggi yang ditunjukkan dengan pergeran puncak yang dipengaruhi oleh adanya ion Co3+ yang menyebabkan terpisahnya charge transfer sepanjang ikatan Co – O – Co. Polycrystalline perovskite manganite Nd0,7Sr0,3Mn(1-x)CoxO3 (x = 0; 0,03; 0,05; 0,07 dan 0,1) material has been synthesized using sol – gel methods. It was observed under the X-ray Diffractometer and shows that different amount of cobalt doping on the sample caused the crystal structure to remains the same, which is orthorhombic with Pnma space group. The characterization using Scanning Electron Microscopy indicated the changed of the grain in the sample which grow larger when cobalt was doped for 3% and 7%, it is due to the lower double exchange (DE) interaction. Furthermore, the result from Vibrating Sampe Magnetometer denote that the magnetization is decreasing caused by the increase amount of cobalt doping in the sample. Moreover, from the cryogenic magnetometer measurement, sample with cobalt doping of 7% shows the high resistivity indicate by the shifting peak which influenced by Co3+ ion that affects the charge transfer integral along the Co – O – Co bond. |
 T-Amilita Medisa Rizky Dharmayanti.pdf :: Unduh
|
| No. Panggil : | T-pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2021 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda. |
| Tipe Konten : | text |
| Tipe Media : | computer |
| Tipe Carrier : | online resource |
| Deskripsi Fisik : | xii, 44 pages : illustration ; appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| T-pdf | 15-22-00726595 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20528126 |